Michilene F8100TL40

About
Michilene F8100TL40 is a Polypropylene Homopolymer (PP Homopolymer) product filled with 40% talc. It is available in North America. Primary characteristic: homopolymer.&&

Product Description
Generic	PP homopolymerization
Material Status	Commercial: Active
Features	Homopolymer
Availabilitys	North America

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.24	g/cm³	ASTM D792
Melt Flow Rate
230℃，2.16kg	8.0	g/10min	ASTM D1238
Shrinkage rate
MD	0.70	%	ASTM D955

MECHANICAL	Nominal value	Unit	Test method
tensile strength
yield	31.0	MPa	ASTM D638
Tensile strain
fracture	10	%	ASTM D638
Bending modulus
tangent	3100	MPa	ASTM D790

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch	37	J/m	ASTM D256

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature			ASTM D648
0.45 MPa, unannealed	135	℃	ASTM D648
1.8 MPa, unannealed	79.4	℃	ASTM D648

Process Conditions
injection	Nominal value	Unit	Test method
Drying temperature	82	°C
Drying time	3.0	hr
Recommended maximum moisture content	0.20	%
Barrel rear temperature	216	°C
Barrel middle temperature	221	°C
Barrel front temperature	227	°C
Nozzle temperature	232	°C
Processing (melt) temperature	227	°C
Mold temperature	43	°C

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.