| About |
|---|
| Minlon® 10B40 BK061是一种40%矿物增强、热稳定的，黑色聚酰胺66树脂，注射成型。 |
| Product Description | |
|---|---|
| Supplier | DuPont |
| Generic | PA66 |
| Material Status | Commercial: Active |
| Features | Heat Stabilized,Glass fiber reinforced |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.51 | g/cm³ | ISO 1183 |
| Shrinkage rate | |||
| MD | 0.40 | % | ISO 294-4，ISO 2577 |
| TD | 0.90 | % | ISO 294-4，ISO 2577 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| fracture | 95.0 | MPa | ISO 527-1-2 |
| Tensile strain | |||
| fracture | 2.5 | % | ISO 527-1/2 |
| Tensile modulus | 10000 | MPa | ISO 527-1-2 |
| Bending modulus | 9500 | MPa | ISO 178 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Linear coefficient of thermal expansion | |||
| MD | 36.0 | µm/m-℃ | ISO 11359-1/-2 |
| TD | 66.0 | µm/m-℃ | ISO 11359-1/-2 |
| Melting temperature | |||
| 10℃ / min | 263 | ℃ | ISO 11357-1/-3 |
| Hot deformation temperature | |||
| 0.45 MPa | 240 | ℃ | ISO 75-1/2 |
| 1.8 MPa | 205 | ℃ | ISO 75-1/2 |
| Flame retardant level | |||
| 0.70 mm | HB | UL 94 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 0.3 | J/cm² | ISO 179/1eA |
| -40℃ | 0.2 | J/cm² | ISO 179/1eA |
| Impact strength of cantilever beam notch | |||
| 23℃ | 3.5 | kJ/m² | ISO 180-1A |
| -40℃ | 2.5 | kJ/m² | ISO 180-1A |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |