| About |
|---|
| Product Description | |
|---|---|
| Supplier | DuPont |
| Generic | PA66 |
| Material Status | Commercial: Negative |
| Features | Heat Stabilized |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Mold shrinkage rate | |||
| parallel | 0.6 | % | ISO 294-4 |
| normal | 0.8 | % | ISO 294-4 |
| Water absorption rate | |||
| 80 mil | 5.4 | % | ISO 62 |
| moisture absorption | |||
| 80 mil | 1.4 | % | ISO 62 |
| Density | 1450 | kg/m³ | ISO 1183 |
| Melt density | 1280 | kg/m³ | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| desiccation | 7500 | MPa | ISO 527-1 |
| moist | 5000 | MPa | ISO 527-2 |
| Fracture stress | |||
| desiccation | 120 | MPa | ISO 527-1 |
| moist | 72 | MPa | ISO 527-2 |
| Fracture strain | |||
| desiccation | 2.5 | % | ISO 527-1 |
| moist | 4 | % | ISO 527-2 |
| Bending modulus | 7000 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 22.8℃ | 3 | kJ/m² | ISO 179/1eA |
| Impact strength of cantilever beam notch | |||
| 22.8℃ | 4 | KJ/m² | ISO 180/1A |
| -40℃ | 3.4 | KJ/m² | ISO 180/1A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting temperature | |||
| 18℉/min | 263 | ℃ | ISO 11357-1/-3 |
| Glass transition temperature | |||
| 18℉/min | 80 | ℃ | ISO 11357-1/-2 |
| Deflection temperature under load | |||
| 260 psi | 230 | ℃ | ISO 75-1/-2 |
| 65 psi | 255 | ℃ | ISO 75-1/-2 |
| Linear coefficient of thermal expansion | |||
| parallel | 41 | ×E-6/K | ISO 11359-1/-2 |
| normal | 62 | ×E-6/K | ISO 11359-1/-2 |
| Relative temperature index | |||
| Electrical characteristics | |||
| 30 mil | 65 | ℃ | UL-746B |
| 60 mil | 65 | ℃ | UL-746B |
| 120 mil | 65 | ℃ | UL-746B |
| Mechanical impact performance | |||
| 30 mil | 65 | ℃ | UL-746B |
| 60 mil | 65 | ℃ | UL-746B |
| 120 mil | 65 | ℃ | UL-746B |
| Non mechanical impact performance | |||
| 30 mil | 65 | ℃ | UL-746B |
| 60 mil | 65 | ℃ | UL-746B |
| 120 mil | 65 | ℃ | UL-746B |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 60 mil | HB | class | IEC 60695-11-10 |
| Thickness testing | 1.5 | mm | IEC 60695-11-10 |
| Flame retardant level | |||
| Thickness is h | HB | class | IEC 60695-11-10 |
| Thickness testing | 0.81 | mm | IEC 60695-11-10 |
| FMVSS flame retardant rating | SE/B | ISO 3795（FMVSS 302） | |
| Burning rate | |||
| Thickness 1 mm | 23 | mm/min | ISO 3795（FMVSS 302） |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Compared to the leakage tracing index | 475 | IEC 60112 |
| Process Conditions | |||
|---|---|---|---|
| Injection molding | Nominal value | Unit | Test method |
| drying temperature | 80 | ℃ | |
| Drying time | 2 – 4 | hr | |
| Processing moisture content | ≤0.2 | % | |
| Optimal melt temperature | 295 | ℃ | |
| Minimum melt temperature | 285 | ℃ | |
| Maximum melt temperature | 305 | ℃ | |
| Spiral tangential maximum speed | 0.2 | m/s | |
| Optimal mold temperature | 100 | ℃ | |
| Minimum mold temperature | 70 | ℃ | |
| Maximum mold temperature | 120 | ℃ | |
| Backpressure range | 50 – 100 | MPa | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |