| About |
|---|
| Miramid® DB1515C is a Polyamide 6 (Nylon 6) material filled with filler. It is available in Europe for injection molding. Primary attribute of Miramid® DB1515C: Mold Release Agent.&& |
| Product Description | |
|---|---|
| Supplier | BASF |
| Generic | PA6 |
| Material Status | Commercial: Active |
| Features | HB |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.35 | g/cm³ | ISO 1183-2 |
| Water absorption rate | ISO 62 2 | ||
| saturated | 6.0 | % | ISO 62-2 |
| balance | 1.8 | % | ISO 62-2 |
| Viscosity number | 150 | cm³/g | ISO 307, 1157, 1628 2 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 6200 | MPa | ISO 527-2 2 |
| tensile strength | |||
| fracture | 120 | MPa | ISO 527-2 2 |
| Tensile strain | |||
| fracture | 3.0 | % | ISO 527-2 2 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA 2 | ||
| -30℃ | 5.00 | kJ/m² | ISO 179/1eA 2 |
| 23℃ | 6.00 | kJ/m² | ISO 179/1eA 2 |
| Charpy impact strength | ISO 179/1eU 2 | ||
| -30℃ | 45.0 | kJ/m² | ISO 179/1eU 2 |
| 23℃ | 45.0 | kJ/m² | ISO 179/1eU 2 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ISO 75-2 2 | ||
| 0.45 MPa | 215 | ℃ | ISO 75-2 2 |
| 1.8 MPa | 200 | ℃ | ISO 75-2 2 |
| Melting temperature | 220 | ℃ | ISO 11357-3 2 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.0E+15 | ohms·cm | IEC 60093 2 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.60 mm | HB | ISO 1210 2 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 3. 18 °F/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |