| Mold Max® 10T, 15T and 27T silicone are water white translucent tin cured silicone rubber compounds that have exceptional tear strength and working properties. They feature Smooth-On’s “Libra®” catalyst for long library life. Mixed 100A:10B by weight, vacuum degassing is recommended for de-airing. Rubber cures overnight at room temperature. Similar in appearance to Smooth-On’s premium Dragon Skin® platinum silicones, Mold Max® ‘T’ silicones are a less costly alternative for creating animatronic skin effects. Mold Max® ‘T’ silicones can be thickened with Thi-Vex® ii thickener for brush-on application and effects. An infinite number of color effects can be achieved by adding Silc Pig® silicone pigments or Cast Magic® effects powders. Mold Max® ‘T’ series silicones are also good for making molds used for casting plaster and wax.&& |
| Product Description | |
|---|---|
| Generic | 硅酮 |
| Material Status | Commercial: Active |
| Features | Good tear strength,Good coloring |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | casting |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.08 | g/cm³ | ASTM D1475 |
| Specific volume | 0.925 | cm³/g | |
| Shrinkage rate | |||
| MD | 0.20 | % | ASTM D2566 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s A | 15 | ASTM D2240 |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| fracture | 3.38 | MPa | ASTM D412 |
| 100% strain | 0.241 | MPa | ASTM D412 |
| Tensile strain | |||
| fracture | 600 | % | ASTM D412 |
| tear strength | 16.5 | kN/m | ASTM D624 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Dielectric strength | > 20 | kV/mm | ASTM D149 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| storage stability | 45 to 55 | min |
| Thermosetting mixed viscosity | Nominal value | Unit | Test method |
|---|---|---|---|
| stripping time | 1400 | min |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Mixing ratio | 100A:10B by weight | ||
| working temperature | -54 to 204 | ℃ |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Die B |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |