| About |
|---|
| Mold Max® 60 is a Shore 60A tin catalyzed silicone rubber formulated for applications requiring high heat resistance (up to 560°F/294°C). It features a low mixed viscosity and cured rubber exhibits very low linear shrinkage. Parts A & B are mixed 100A & 3B by weight. Pot life is 40 minutes and cure time is 24 hours. Applications include making foundry patterns, flat pattern reproductions and casting low-melt metal alloys such as tin and pewter. PLEASE NOTE: THI-VEX® Silicone Thickener is NOT recommended for use with Mold Max® 60.&& |
| Product Description | |
|---|---|
| Generic | 硅酮 |
| Material Status | Commercial: Active |
| Features | Low Viscosity,Low contractility,High Heat Resistance |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | casting |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.45 | g/cm³ | ASTM D1475 |
| Specific volume | 0.690 | cm³/g | |
| Shrinkage rate | |||
| MD | 0.15 | % | ASTM D2566 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s A | 60 | ASTM D2240 |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| fracture | 2.74 | MPa | ASTM D412 |
| 100% strain | 2.28 | MPa | ASTM D412 |
| Tensile strain | |||
| fracture | 130 | % | ASTM D412 |
| tear strength | 11.0 | kN/m | ASTM D624 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 9.0E+14 | ohms·cm | ASTM D257 |
| Dielectric strength | > 20 | kV/mm | ASTM D149 |
| Dielectric constant | |||
| 100 Hz | 3.40 | ASTM D150 | |
| Dissipation factor | |||
| 100 Hz | 0.020 | ASTM D150 |
| Thermosetting mixed viscosity | Nominal value | Unit | Test method |
|---|---|---|---|
| stripping time | |||
| 23℃ | 1400 | min |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Mixing ratio | 100A:3B by weight | ||
| working temperature | -54 to 293 | ℃ |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Thermal conductivity coefficient | 0.050 | W/m/K | ASTM C177 |
| storage stability | |||
| 23℃ | 40 | min | ASTM D2471 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Die B |
| 3. Cure Time |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |