| MonoSol M1030 is a PVOH based thermoplastic film, soluble in hot water and manufactured using MonoSol’s proprietary solution cast technology. MonoSol M1030 is a hot water-soluble general purpose PVOH film. With high elongation, M1030 performs well in molding and vacuum bag operations. The maximum use temperature is 275 F (135 C). Standard thicknesses are 38 micron (1.5 mil), 51 micron (2.0 mil) and 76 micron (3.0 mil).&& |
| Product Description | |
|---|---|
| Generic | PVOH |
| Material Status | Commercial: Active |
| Features | Biodegradable,Good Tensile Strength,Water soluble |
| Availabilitys | North America,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| water content | |||
| 23℃ | 6.1 | % | |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 76 | µm | |
| film thickness | 38 µm, 51 µm, and 76 µm | ||
| Secant modulus | |||
| 100%，MD，76 µm | 21.4 | MPa | ASTM D882, ISO 527-3 |
| tensile strength | |||
| MD, fracture, 76 µ m | 55.8 | MPa | ASTM D882 |
| MD，76 µm | 55.8 | MPa | ISO 527-3 |
| Tensile strain | |||
| MD, fracture, 76 µ m | 490 | % | ASTM D882, ISO 527-3 |
| Elmandorf Tear Strength – MD | |||
| 76 µm | 400 | g | ASTM D1922 |
| 76 µm | 0.041 | N | ISO 6383-2 |
| dosage | |||
| 76.0 µm | 10.3 | m²/kg | ASTM D4321 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Continuous use temperature | 135 | ℃ |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 50%RH |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |