| About |
|---|
| MonoSol M2000 is a PVOH based thermoplastic film, soluble in hot water and manufactured using MonoSol’s proprietary solution cast technology. MonoSol M2000 is a hot water-soluble general purpose PVOH film. With high stiffness and strength, M2000 performs well in continuous molding operations. The maximum use temperature is 275 F (135 C). Standard thickness is 38 micron (1.5 mil).&& |
| Product Description | |
|---|---|
| Generic | PVOH |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Biodegradable,Water soluble |
| Availabilitys | North America,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| water content | |||
| 23℃，38 µm | 6.0 | % | |
| solubility | |||
| Disintegration：60℃ | 18.0 | sec | |
| Dissolution：60℃ | 68.0 | sec | |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 38 | µm | |
| film thickness | 38 µm | ||
| tensile strength | |||
| MD, yield, 38 µ m | 75.8 | MPa | ASTM D882 |
| MD, yield, 38 µ m | 75.8 | MPa | ISO 527-3 |
| Tensile strain | |||
| MD, yield, 38 µ m | 3.0 | % | ASTM D882 , ISO 527-3 |
| dosage | |||
| 23℃，38.0 µm | 100 | MPa | ASTM D4321 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Continuous use temperature | 135 | ℃ |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 50%RH |
| 3. Distilled Water (MSTM 205) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |