| Monprene OM-10240 is a specialty thermoplastic elastomer, available in NAT, BLK, and colors, designed for overmolding applications like grips and anti-skid parts for consumer and industrial products. Monprene OM-10240 is a low hardness, medium density, UV stabilized, opaque grade that exhibits excellent adhesion to PC, ABS, and PC/ABS.&& |
| Product Description | |
|---|---|
| Supplier | Teknor Apex |
| Generic | TPE |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Low liquidity,Smoothness,Good bond,Lubricating,Low Hardness |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.978 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 2.0 | g/10min | ASTM D1238 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | ASTM D2240 | ||
| Shore A, 1 second | 35 | ||
| Shore A, 1 second, injection molding | 43 | ||
| Shore A, 5 seconds, injection molding | 40 |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | ASTM D412 | ||
| TD, 100% strain | 1.48 | MPa | |
| MD, 100% strain | 1.61 | MPa | |
| TD, 300% strain | 3.16 | MPa | |
| MD, 300% strain | 3.41 | MPa | |
| tensile strength | ASTM D412 | ||
| TD, fracture | 5.18 | MPa | |
| MD, fracture | 4.83 | MPa | |
| Tensile strain | ASTM D412 | ||
| TD, fracture | 470 | % | |
| Flow rate, fracture | 450 | % | |
| tear strength | ASTM D624 | ||
| TD | 21.9 | kN/m | |
| MD | 21.4 | kN/m | |
| Compression deformation | ASTM D395B | ||
| 23℃，22 hr | 39 | % | |
| 70℃，22 hr | 80 | % |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Adhesion to ABS | |||
| Adhesion to PC | |||
| Adhesion to PC/ABS |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Extrusion | Nominal value | Unit | Test method |
| Drying temperature | 60.0 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Barrel rear temperature | 138 to 160 | °C | |
| Barrel middle temperature | 182 to 199 | °C | |
| Barrel front temperature | 182 to 199 | °C | |
| Nozzle temperature | 193 to 210 | °C | |
| Processing (melt) temperature | 177 to 199 | °C | |
| Mold temperature | 4.44 to 32.2 | °C | |
| Injection pressure | 1.38 to 5.52 | MPa | |
| Back pressure | 0.172 to 0.862 | MPa | |
| Screw speed | 50 to 100 | rpm | |
| Cushion | 3.81 to 25.4 | mm | |
| Barrel 1 zone temperature | 138 to 149 | °C | |
| Barrel 2 zone temperature | 149 to 160 | °C | |
| Barrel 3 zone temperature | 160 to 182 | °C | |
| Barrel 5 zone temperature | 171 to 193 | °C | |
| Nozzle temperature | 182 to 204 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Die C, 20 in/min |
| 3. Type 1 |
| 4. Aged for 48 hr |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |