| Monprene OM-10250 is designed for overmolding applications like grips and anti-skid parts for consumer products. Monprene OM-10250 is a medium density, medium hardness, opaque grade that exhibits excellent adhesion to PC, ABS, and PC/ABS.&& |
| Product Description | |
|---|---|
| Supplier | Teknor Apex |
| Generic | TPE |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Low liquidity,Smoothness,Ultraviolet absorption,Lubricating |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.05 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 2.0 | g/10min | ASTM D1238 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | ASTM D2240 | ||
| Shaw’s A | 54 | ASTM D2240 | |
| Shore A, 5 seconds | 50 | ASTM D2240 |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | ASTM D412 | ||
| TD, 100% strain | 1.98 | MPa | ASTM D412 |
| MD, 100% strain | 2.16 | MPa | ASTM D412 |
| TD, 300% strain | 3.17 | MPa | ASTM D412 |
| MD, 300% strain | 3.58 | MPa | ASTM D412 |
| tensile strength | ASTM D412 | ||
| TD, fracture | 5.27 | MPa | ASTM D412 |
| MD, fracture | 4.63 | MPa | ASTM D412 |
| Tensile strain | ASTM D412 | ||
| TD, fracture | 620 | % | ASTM D412 |
| Flow rate, fracture | 520 | % | ASTM D412 |
| tear strength | ASTM D624 | ||
| TD | 27.7 | kN/m | ASTM D624 |
| MD | 26.8 | kN/m | ASTM D624 |
| Compression deformation | ASTM D395B | ||
| 23℃，22 hr | 25 | % | ASTM D395B |
| 70℃，22 hr | 86 | % | ASTM D395B |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Adhesion to ABS | |||
| Adhesion to PC | |||
| Adhesion to PC/ABS |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 66 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Barrel rear temperature | 138 to 188 | °C | |
| Barrel middle temperature | 154 to 199 | °C | |
| Barrel front temperature | 154 to 216 | °C | |
| Nozzle temperature | 154 to 221 | °C | |
| Processing (melt) temperature | 166 to 221 | °C | |
| Mold temperature | 10 to 32 | °C | |
| Injection pressure | 1.38 to 6.89 | MPa | |
| Injection speed | 快速 | ||
| Back pressure | 0.172 to 0.862 | MPa | |
| Screw speed | 50 to 120 | rpm | |
| Cushion | 3.81 to 25.4 | mm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Die C, 20 in/min |
| 3. Type 1 |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |