| About |
|---|
| Sarlink OM-12250-01 is designed for overmolding applications for the consumer industry. Monprene OM-12250-01 is a medium density, medium hardness, opaque grade suitable for both injection molding and extrusion.&& |
| Product Description | |
|---|---|
| Supplier | Teknor Apex |
| Generic | TPE |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Low liquidity,Ultraviolet absorption,Agglomerability |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.968 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 2.0 | g/10min | ASTM D1238 |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | ASTM D412 | ||
| TD, 100% strain | 1.67 | MPa | ASTM D412 |
| MD, 100% strain | 2.04 | MPa | ASTM D412 |
| tensile strength | ASTM D412 | ||
| TD, 300% strain | 2.88 | MPa | ASTM D412 |
| MD, 300% strain | 3.30 | MPa | ASTM D412 |
| tensile strength | ASTM D412 | ||
| fracture | 7.72 | MPa | ASTM D412 |
| MD, fracture | 7.58 | MPa | ASTM D412 |
| Tensile strain | ASTM D412 | ||
| fracture | 670 | % | ASTM D412 |
| Flow rate, fracture | 670 | % | ASTM D412 |
| tear strength | ASTM D624 | ||
| TD | 30.1 | kN/m | ASTM D624 |
| MD | 28.4 | kN/m | ASTM D624 |
| Compression deformation | ASTM D395B | ||
| 23℃，22 hr | 18 | % | ASTM D395B |
| 70℃，22 hr | 65 | % | ASTM D395B |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | ASTM D2240 | ||
| Shore A, 1 second, injection molding | 52 | ASTM D2240 | |
| Shore A, 1 second, injection molding | 62 | ASTM D2240 | |
| Shore A, 5 seconds, injection molding | 60 | ASTM D2240 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Adhesion to ABS | |||
| Adhesion to PC | |||
| Adhesion to PC/ABS |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Extrusion | Nominal value | Unit | Test method |
| Drying temperature | 60 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Barrel rear temperature | 160 to 193 | °C | |
| Barrel middle temperature | 160 to 193 | °C | |
| Barrel front temperature | 160 to 193 | °C | |
| Nozzle temperature | 160 to 193 | °C | |
| Processing (melt) temperature | 160 to 193 | °C | |
| Mold temperature | 16 to 32 | °C | |
| Injection pressure | 1.38 to 5.52 | MPa | |
| Back pressure | 0.172 to 0.862 | MPa | |
| Screw speed | 50 to 100 | rpm | |
| Cushion | 3.81 to 25.4 | mm | |
| Barrel 1 zone temperature | 160 to 182 | °C | |
| Barrel 2 zone temperature | 160 to 182 | °C | |
| Barrel 3 zone temperature | 160 to 182 | °C | |
| Barrel 4 zone temperature | 160 to 182 | °C | |
| Barrel 5 zone temperature | 160 to 182 | °C | |
| Nozzle temperature | 160 to 182 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Die C, 20 in/min |
| 3. Type 1 |
| 4. Aged for 48 hr |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |