| About |
|---|
| Monprene SP-19947 is a high performance thermoplastic elastomer designed for a variety of consumer product applications including sporting goods. Monprene SP-19947 is a low hardness, low density medium flow UV stabilized grade that is designed for injection molding but can be extruded.&& |
| Product Description | |
|---|---|
| Supplier | Teknor Apex |
| Generic | TPE |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Excellent Processability,Good flexibility,Smoothness,Good bond,Lubricating,Elastic,Low density,Moderate liquidity,Low Hardness,Solvent resistance,Good coloring |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.888 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 3.0 | g/10min | ASTM D1238 |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | ASTM D412 | ||
| TD, 100% strain | 1.30 | MPa | ASTM D412 |
| MD, 100% strain | 1.85 | MPa | ASTM D412 |
| tensile strength | ASTM D412 | ||
| TD, 300% strain | 1.96 | MPa | ASTM D412 |
| MD, 300% strain | 2.47 | MPa | ASTM D412 |
| tensile strength | ASTM D412 | ||
| fracture | 6.74 | MPa | ASTM D412 |
| MD, fracture | 3.23 | MPa | ASTM D412 |
| Tensile strain | ASTM D412 | ||
| fracture | 790 | % | ASTM D412 |
| Flow rate, fracture | 540 | % | ASTM D412 |
| tear strength | ASTM D624 | ||
| TD | 24.3 | kN/m | ASTM D624 |
| MD | 20.1 | kN/m | ASTM D624 |
| Compression deformation | ASTM D395B | ||
| 23℃，22 hr | 20 | % | ASTM D395B |
| 70℃，22 hr | 48 | % | ASTM D395B |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | ASTM D2240 | ||
| Shore A, 1 second, injection molding | 50 | ASTM D2240 | |
| Shore A, 5 seconds, injection molding | 47 | ASTM D2240 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Extrusion | Nominal value | Unit | Test method |
| Barrel rear temperature | 182 to 232 | °C | |
| Barrel middle temperature | 188 to 238 | °C | |
| Barrel front temperature | 193 to 243 | °C | |
| Nozzle temperature | 199 to 249 | °C | |
| Processing (melt) temperature | 199 to 249 | °C | |
| Mold temperature | 35 to 49 | °C | |
| Injection pressure | 1.38 to 5.52 | MPa | |
| Injection speed | Fast | ||
| Back pressure | 0.172 to 0.689 | MPa | |
| Screw speed | 50 to 100 | rpm | |
| Cushion | 3.81 to 25.4 | mm | |
| Barrel 1 zone temperature | 182 to 232 | °C | |
| Barrel 2 zone temperature | 188 to 238 | °C | |
| Barrel 3 zone temperature | 193 to 243 | °C | |
| Barrel 4 zone temperature | 193 to 243 | °C | |
| Barrel 5 zone temperature | 199 to 249 | °C | |
| Nozzle temperature | 199 to 249 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Die C, 20 in/min |
| 3. Type 1 |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |