| Moplen EP300K Moplen EP300K is a low fluidity impact copolymer suitable for injection moulding applications. The product exhibits very high impact strength even at low temperature combined with a good stiffness. Moplen EP300K is typically used by customers in a wide range of applications including houseware items and crates.&&Moplen EP300K “Moplen” EP300K is a low fluidity heterophasic copolymer, suitable for injection moulding applications. The product exhibits very high impact even at low temperature combined with a good stiffness. “Moplen” EP300K is typically used in houseware items and in crates. Moplen EP300K resin meets the FDA requirements in the Code of Federal Regulations in 21 CFR 177.1520 for food contact.&&Moplen EP300K Moplen EP300K is a medium flow, hetrophasic polypropylene copolymer mainly designed for injection moulding applications. Moplen EP300K combines good process ability with very high impact and good stiffness. Because of its high mechanical properties, Moplen EP300K is widely used for injection moulding medium sized containers, buckets, pails, transport crates and crates for cold storage. Other typical applications of Moplen EP300K are injection moulded components for small appliances, component for industrial applications and parts for the automotive industry (e.g. wheel arch liners, steering wheels and interior parts). Moplen EP300K is further suitable for house wares, seats, chair shells, toys, suitcases and small packaging items. Thermoforming multilayer container for dairy products is also an important application of Moplen EP300K. * Moplen EP300K is suitable for food contact.&& |
| Product Description | |
|---|---|
| Supplier | LyondellBasell |
| Generic | PP homopolymerization |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Low warping,Excellent Processability,Low liquidity,High impact resistance,Food contact compliance,Moderate liquidity,Copolymer,low-temperature impact resistance,Impact copolymer |
| Availabilitys | Africa & Middle East ,Asia Pacific,Europe |
| Process Methods | Thermo forming |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.900 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 4.0 | g/10min | ISO 1133 |
| Melt Volume Rate | |||
| 230℃，2.16 kg | 5.40 | cm³/10min | ISO 1133 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20℃ | 4.0 | kJ/m² | ISO 179/1eA |
| 0℃ | 5.5 | kJ/m² | ISO 179/1eA |
| 23℃ | 11 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | ISO 179/1eU | ||
| -20℃ | 80 | kJ/m² | ISO 179/1eU |
| 0℃ | 140 | kJ/m² | ISO 179/1eU |
| 23℃ | 无断裂 | ISO 179/1eU |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 75.0 | ℃ | ISO 75-2/B |
| Vicat Softening Temp | |||
| A50 | 150 | ℃ | ISO 306/A50 |
| B50 | 71.0 | ℃ | ISO 306 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Ball hardness | |||
| H358/30 | 53.0 | MPa | ISO 2039-1 |
| Tensile modulus | 1200 | MPa | ISO 527-2 |
| tensile strength | |||
| yield | 27.0 | MPa | ISO 527-2 |
| Tensile strain | ISO 527-2 | ||
| yield | 7.0 | % | ISO 527-2 |
| fracture | > 50 | % | ISO 527-2 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Loading 1 (10 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |