Moplen EP310D - SOLIAO

About
Moplen EP310D Moplen EP310D is a low fluidity polypropylene heterophasic copolymer. It does not contain anti-blocking and slip additives. Moplen EP310D is typically used by customers for extrusion applications when high mechanical properties are of the utmost importance. It is normally extruded by customers in single layer film for lamination on other substrates, obtaining structures that can be processed under high retorting conditions. This grade has been reported to be used in some other typical applications, such as extruded film for adhesive tapes, lamination film, freezer film, pipes, fittings and containers produced by extrusion blow molding. Customers also reported that can be used as a building block for heavy duty bags, delivering high impact and thermal resistance over a broad range of temperatures. Moplen EP310D has been reported by customers to exhibit high impact, good puncture, good tear resistance, high seal strength and seal integrity.&&Moplen EP310D High Melt Strength Polypropylene Impact Copolymer Resin Features: Excellent processability for extension and blow molding Very good cold impact resistance Very high impact strength and good stiffness Applications: Blown film for Heavy Duty Bag Pipe (non Pressure) and Profile Corrugated pipe Blow Molding Bottle Thermoforming Sheet&&

About

Moplen EP310D Moplen EP310D is a low fluidity polypropylene heterophasic copolymer. It does not contain anti-blocking and slip additives. Moplen EP310D is typically used by customers for extrusion applications when high mechanical properties are of the utmost importance. It is normally extruded by customers in single layer film for lamination on other substrates, obtaining structures that can be processed under high retorting conditions. This grade has been reported to be used in some other typical applications, such as extruded film for adhesive tapes, lamination film, freezer film, pipes, fittings and containers produced by extrusion blow molding. Customers also reported that can be used as a building block for heavy duty bags, delivering high impact and thermal resistance over a broad range of temperatures. Moplen EP310D has been reported by customers to exhibit high impact, good puncture, good tear resistance, high seal strength and seal integrity.&&Moplen EP310D High Melt Strength Polypropylene Impact Copolymer Resin Features: Excellent processability for extension and blow molding Very good cold impact resistance Very high impact strength and good stiffness Applications: Blown film for Heavy Duty Bag Pipe (non Pressure) and Profile Corrugated pipe Blow Molding Bottle Thermoforming Sheet&&

Product Description
Supplier	LyondellBasell
Generic	PP homopolymerization
Material Status	Commercial: Active
Features	Excellent Processability,Low liquidity,Food contact compliance,Impact copolymer
Availabilitys	Africa & Middle East ,Asia Pacific,Europe

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.900	g/cm³	ISO 1183
Melt Flow Rate
230℃，2.16kg	0.95	g/10min	ISO 1133

MECHANICAL	Nominal value	Unit	Test method
tensile strength
yield	26.0	MPa	ISO 527-2/50
fracture	30.0	MPa	ISO 527-2
Tensile strain			ISO 527-2/50
yield	13	%	ISO 527-2/50
fracture	> 500	%	ISO 527-2/50
Bending modulus	1050	MPa	ISO 178

film	Nominal value	Unit	Test method
tensile strength			ASTM D882
MD, fracture, 50 µ m, blow molded film	55.0	MPa	ASTM D882
TD, fracture, 50 µ m, blow molded film	45.0	MPa	ASTM D882
Tensile strain			ASTM D882
MD, fracture, 50 µ m, extruded film	1000	%	ASTM D882
TD, fracture, 50 µ m, extruded film	1100	%	ASTM D882
Drop hammer impact
Casting thin film	> 1500	g	ASTM D1709

IMPACT	Nominal value	Unit	Test method
Charpy Notched Impact Strength			ISO 179/1eA
-20℃	6.0	kJ/m²	ISO 179/1eA
23℃	70	kJ/m²	ISO 179/1eA

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
0.45 MPa, unannealed	80.0	℃	ISO 75-2/B
Vicat Softening Temp
A50	150	℃	ISO 306/A50

optical performance	Nominal value	Unit	Test method
gloss
50 µ m, cast thin film	21		ASTM D2457
Haze
50 µ m, cast thin film	38	%	ASTM D1003

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.