About
Moplen HP400H Moplen HP400H is a homopolymer for extrusion and compounding applications. Moplen HP400H exhibits easy processability and a good stiffness/impact balance at ambient temperature. It is typically used by customers in applications such as: thermoformed tubs, containers, medium draw trays and blister packs, flowerpots and small extrusion blow moulded bottles.&&Moplen HP400H General Purpose Polypropylene Homopolymer Resin Features: Good processability Low odor and taste transfer Excellent chemical resistance Low yellowness Good tensile strength Applications: Slit tape Straw Monofilaments Rope, twine Stationary sheets Bottles, flasks&&

About

Moplen HP400H Moplen HP400H is a homopolymer for extrusion and compounding applications. Moplen HP400H exhibits easy processability and a good stiffness/impact balance at ambient temperature. It is typically used by customers in applications such as: thermoformed tubs, containers, medium draw trays and blister packs, flowerpots and small extrusion blow moulded bottles.&&Moplen HP400H General Purpose Polypropylene Homopolymer Resin Features: Good processability Low odor and taste transfer Excellent chemical resistance Low yellowness Good tensile strength Applications: Slit tape Straw Monofilaments Rope, twine Stationary sheets Bottles, flasks&&

Product Description
Supplier	LyondellBasell
Generic	PP homopolymerization
Material Status	Commercial: Active
Features	Good Rigidity,Excellent Processability,High impact resistance,Low odor,Good Tensile Strength,Solvent resistance,Homopolymer
Availabilitys	Africa & Middle East ,Asia Pacific,Europe
Process Methods	Extrusion

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.900	g/cm³	ASTM D792 , ISO 1183/D
Melt Flow Rate
230℃，2.16kg	2.1	g/10min	ASTM D1238
230℃，2.16kg	2.0	g/10min	ISO 1133
Melt Volume Rate
230℃，2.16 kg	2.70	cm³/10min	ISO 1133

IMPACT	Nominal value	Unit	Test method
Charpy Notched Impact Strength
23℃	4.0	kJ/m²	ISO 179/1eA
Charpy Unnotch Impact strength			ISO 179/1eU
0℃	90	kJ/m²	ISO 179/1eU
23℃	无断裂		ISO 179/1eU
Impact strength of cantilever beam notch
23℃	40	J/m	ASTM D256

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
0.45 MPa, unannealed	95.0	℃	ASTM D648
0.45 MPa, unannealed	80.0	℃	ISO 75-2/B
Vicat Softening Temp
A50	150	℃	ISO 306/A50
B50	80.0	℃	ISO 306

optical performance	Nominal value	Unit	Test method
gloss
60°	107		ASTM D2457
Haze
1000 µm	45	%	ASTM D1003

MECHANICAL	Nominal value	Unit	Test method
Ball hardness
H358/30	70.0	MPa	ISO 2039-1
Tensile modulus	1400	MPa	ISO 527-2
tensile strength
yield	33.0	MPa	ASTM D638
yield	34.0	MPa	ISO 527-2
Tensile strain
yield	11	%	ASTM D638 , ISO 527-2
fracture	> 50	%	ISO 527-2
Bending modulus	1450	MPa	ASTM D790

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.