| About |
|---|
| Mosten GB 506 is a polypropylene produced by Unipetrol RPA using INNOVENE™ PP gas-phase technology. Characteristics: nucleation SVHC-phthalates free meets EN 71-3/9 Safety of toys meets European Pharmacopoeia 8 (Ph. Eur. 8, 3.1.3) International Designation: ISO 19069-PP-B,,GM,16-45-045 Application: technical parts co-extrusion of films compounds&& |
| Product Description | |
|---|---|
| Generic | PP homopolymerization |
| Material Status | Commercial: Active |
| Features | High impact resistance,Food contact compliance,Block Copolymer,Crystal |
| Availabilitys | Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Melt Flow Rate | |||
| 230℃，2.16kg | 6.0 | g/10min | ISO 1133 |
| Shrinkage rate | ISO 294-4 | ||
| TD | 2.3 | % | ISO 294-4 |
| MD | 1.9 | % | ISO 294-4 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 63 | ISO 868 | |
| Tensile modulus | 1500 | MPa | ISO 527-2 |
| tensile strength | |||
| yield | 29.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | 100 | % | ISO 527-2 |
| yield | 5.0 | % | ISO 527-2 |
| Tensile Creep Modulus（1 hr） | 1100 | MPa | ISO 899-1 |
| Tensile creep modulus | |||
| 1000 hr | 580 | MPa | ISO 899-1 |
| Bending modulus | 1500 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1 | ||
| -20℃ | 4.0 | kJ/m² | ISO 179/1 |
| 23℃ | 11 | kJ/m² | ISO 179/1 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 57.0 | ℃ | ISO 75-2/A |
| Vicat Softening Temp | 154 | ℃ | ISO 306 |
| Melting temperature | 165 to 170 | ℃ | ISO 11357-3 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Processing (melt) temperature | 200 to 280 | °C | |
| Mold temperature | 20 to 60 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |