| About |
|---|
| Product Description | |
|---|---|
| Supplier | TEIJIN |
| Generic | PC+ABS |
| Material Status | Commercial: Active |
| Features | halogen-free,High liquidity,Flame Characteristics,High rigidity |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.21 | g/cm³ | ISO 1183 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile Strength | |||
| yld | 61 | MPa | ISO 527-2 |
| brk | 44 | MPa | ISO 527-2 |
| Tensile Strain | |||
| brk | 43 | % | ISO 527 |
| Flexural Modulus | 3300 | MPa | ISO 178 |
| Flexural Strength | 98 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy notched Impact strength | 20 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact strength | NB | ISO 179 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| HDT | |||
| 1.80 MPa，Unannealed | 81 | ℃ | ISO 75-1/-2 |
| Ball Pressure Test | 合格 | IEC 60695-10-2 | |
| Relative Temp Index(RTI) | |||
| elec | 85 | ℃ | UL-746B |
| Imp | 85 | ℃ | UL-746B |
| Str | 85 | ℃ | UL-746B |
| ELECTRICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Comparative Tracking Index | 2 | PLC Code | UL 746 |
| HAI | |||
| 1.2 mm | 3 | PLC Code | UL 746A |
| 1.5 mm | 3 | PLC Code | UL 746A |
| 2.0 mm | 2 | PLC Code | UL 746A |
| 3.0 mm | 2 | PLC Code | UL 746A |
| Hot Wire Ignition | |||
| 1.2 mm | 3 | PLC Code | UL 746A |
| 1.5 mm | 3 | PLC Code | UL 746A |
| 2.0 mm | 3 | PLC Code | UL 746A |
| 3.0 mm | 2 | PLC Code | UL 746A |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame Class Rating | |||
| 0.7 mm | V-2 | UL 94 | |
| 1.0 mm | V-0 | UL 94 | |
| 2.0 mm | 5VB | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection molding | Nominal value | Unit | Test method |
| drying temperature | 80 | ℃ | |
| Drying time | 5-8 | hr | |
| Melt Temperature | 230-270 | ℃ | |
| Mold temperature | 50-70 | ℃ | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |