MV00ASUV_WH9D703

About
LNP* Verton* Compound MV00ASUV_WH9D703是用50％长纤维单色颗粒填充PP的化合物。

Product Description
Supplier	SABIC
Generic	PP not specified
Material Status	Commercial: Active
Features	Good Rigidity,Good flexibility,High impact resistance,Good wear resistance
Availabilitys	North America

Technical Data
MECHANICAL	Nominal value	Unit	Test method
tensile strength
Fracture, 5 mm/min	163	MPa	ISO 527
屈服，5mm/min	136	MPa	ISO 527
Tensile strain
Fracture, 5 mm/min	1.9	%	ISO 527
屈服，5mm/min	1.9	%	ISO 527
Tensile modulus
1 mm/min	8830	MPa	ISO 527
bending strength
Fracture, 2 mm/min	199	MPa	ISO 178
Bending modulus
2 mm/mim	9430	MPa	ISO 178

IMPACT	Nominal value	Unit	Test method
Instrument impact energy peak
23℃	76	cm-kgf	ASTM D 3763
Total energy of instrument impact
23℃	118	cm-kgf	ASTM D 3763
Notched impact strength of cantilever beam
23℃，80104	53	kJ/m²	ISO 180/1U
Impact strength of cantilever beam notch
80104，-40℃	22	kJ/m²	ISO 180-1A
23℃，80104	22	kJ/m²	ISO 180-1A

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
1.8 MPa, unannealed, 64 mm span	153	℃	ISO 75/Af

PHYSICAL	Nominal value	Unit	Test method
Density	1.35	g/cm³	ASTM D792

Process Conditions
injection molding	Nominal value	Unit	Test method
Drying temperature	80	℃
Drying time	4	hrs
Melt temperature	220-250	℃
Front temperature	250-260	℃
Mid section temperature	245-255	℃
Post stage temperature	230-245	℃
Mold temperature	40-65	℃
Back pressure	0.2-0.2	MPa
Screw speed	30-60	rpm

Notes
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.