| About |
|---|
| Product Description | |
|---|---|
| Generic | ASA |
| Material Status | Commercial: Active |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | |||
| 23℃ | 1.07 | g/cm³ | GB/T1033-1986 |
| Melt Flow Rate | |||
| 220℃，10.0kg | 12 | g/10min | GB/T3682-2000 |
| Shrinkage rate | 0.6-0.8 | % | GB/T15585-1995 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| 50mm/min | 42 | Mpa | GB/T1040-1992 |
| Tensile strain | |||
| Fracture, 50mm/min | >25 | % | |
| bending strength | |||
| 2mm/min | 72 | Mpa | GB/T9341-2000 |
| Bending modulus | 2150 | Mpa | GB/T9341-2000 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Notched impact strength of cantilever beam | 60 | kJ/m² | GB/T1843-1996 |
| Impact strength of cantilever beam notch | 17 | kJ/m² | GB/T1843-1996 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.82Mpa | 95 | ℃ | GB/T1634.1-2004 |
| High temperature long-term usage temperature | 90 | ℃ | |
| Low temperature for long-term use | -25 | ℃ |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 3.2mm | HB | UL-94 |
| Process Conditions | |||
|---|---|---|---|
| Injection molding | Nominal value | Unit | Test method |
| drying temperature | 90 | ℃ | |
| Drying time | 2 | h | |
| Rear section of barrel temperature | 205-210 | ℃ | |
| Middle section of barrel temperature | 210-220 | ℃ | |
| Front section of barrel temperature | 210-220 | ℃ | |
| Nozzle temperature | 210-220 | ℃ | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |