| About |
|---|
| NANCAR® 1043 is a medium acrylonitrile butadiene copolymer with medium oil resistance. It is polymerized at low temperature and contains sufficient antioxidant for normal aging conditions. It has high Mooney viscosity and provides compounds with higher strength and modulus. NANCAR® 1043 is recommended for use in applications requiring improved low temperature properties. NANCAR ® 1043 provides excellent extrusion and general processing improvement.&& |
| Product Description | |
|---|---|
| Supplier | Nantex |
| Generic | NBR |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Excellent Processability,Inoxidizability,Copolymer,Grease resistance |
| Availabilitys | Asia Pacific |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.970 | g/cm³ | |
| Mooney viscosity | |||
| ML 1+4，100℃ | 83 | MU | ASTM D1646 |
| Acrylonitrile content (Bound) | 33.0 | % | Internal Method |
| Stabilizer | Slightly-staining | ||
| solubility | |||
| in MEK | 100 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | ASTM D2240 | ||
| Shaw’s A | 67 | ASTM D2240 | |
| Shaw’s A | 68 | ASTM D2240 | |
| Shaw’s A | 69 | ASTM D2240 |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | ASTM D412 | ||
| 300% strain | 10.9 | MPa | ASTM D412 |
| 300% strain | 11.5 | MPa | ASTM D412 |
| 300% strain | 12.7 | MPa | ASTM D412 |
| tensile strength | ASTM D412 | ||
| yield | 23.4 | MPa | ASTM D412 |
| yield | 23.9 | MPa | ASTM D412 |
| yield | 24.6 | MPa | ASTM D412 |
| Tensile strain | ASTM D412 | ||
| fracture | 550 | % | ASTM D412 |
| fracture | 520 | % | ASTM D412 |
| fracture | 500 | % | ASTM D412 |
| tear strength | 50.0 | kN/m | ASTM D624 |
| Compression deformation | |||
| 100℃，70 hr | 55 | % | ASTM D395 |
| Aging performance | Nominal value | Unit | Test method |
|---|---|---|---|
| The rate of change in tensile strength in air | |||
| 100℃，70 hr | -4.0 | % | ASTM D865 |
| The rate of change in ultimate elongation in air | |||
| 100℃，70 hr | -25 | % | ASTM D865 |
| The rate of change in hardness of a hardness tester in the air | |||
| Shore A, 100 ℃, 70 hr | 5.0 | ASTM D865 | |
| The rate of change in tensile strength | ASTM D471 | ||
| 100 ℃, 70 hr, in ASTM # 1 oil | -5.0 | % | ASTM D471 |
| 100 ℃, 70 hr, in ASTM # 3 oil | -21 | % | ASTM D471 |
| Change rate of ultimate elongation | ASTM D471 | ||
| 100 ℃, 70 hr, in ASTM # 1 oil | -22 | % | ASTM D471 |
| 100 ℃, 70 hr, in ASTM # 3 oil | -21 | % | ASTM D471 |
| The rate of change in Shore hardness | ASTM D471 | ||
| Support A, 100 ℃, 70 hr, in ASTM # 1 oil | 1.0 | ASTM D471 | |
| Support A, 100 ℃, 70 hr, in ASTM # 3 oil | -12 | ASTM D471 | |
| Volume change | ASTM D471 | ||
| 100 ℃, 70 hr, ASTM standard oil (No.1) | 1.0 | % | ASTM D471 |
| 100 ℃, 70 hr, ASTM standard oil (No.3) | 22 | % | ASTM D471 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Heat loss | 0.40 | % | ASTM D5688 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Cured for 20.0 min at 302°F |
| 3. Cured for 40.0 min at 302°F |
| 4. Cured for 60.0 min at 302°F |
| 5. Cured for 60.0 min at 150°C |
| 6. Cured for 40.0 min at 150°C |
| 7. Cured for 20.0 min at 150°C |
| 8. Die C |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |