| NANCAR® 1203D is a dry blend of 70 parts NANCAR NBR and 30 parts polyvinyl chloride. This polymer has sufficient stabilizer for normal aging conditions. It can be processed by normal mixing procedures. Its good processability for extrusion provides smooth surface on the resultant products. NANCAR® 1203D has excellent resistance to abrasion, ozone, oils, fuels and solvents. It is suggested for use in cable jackets, belts, hose covers, shoe soles, rolls and sponge applications.&& |
| Product Description | |
|---|---|
| Supplier | Nantex |
| Generic | NBR |
| Material Status | Commercial: Active |
| Features | Excellent Processability,Good surface appearance,Good stability,Good wear resistance,Grease resistance,Ozone resistance |
| Availabilitys | Asia Pacific |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Mooney viscosity | |||
| ML 1+4，100℃ | 62 | MU | ASTM D1646 |
| Acrylonitrile content (Bound) | 33.0 | % | Internal Method |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s A | 73 |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| yield | 14.0 | MPa | |
| Tensile strain | |||
| fracture | 460 | % | |
| Compression deformation | |||
| 100℃，70 hr | 46 | % |
| Aging performance | Nominal value | Unit | Test method |
|---|---|---|---|
| The rate of change in tensile strength in air | |||
| 100℃，70 hr | 10 | % | |
| The rate of change in ultimate elongation in air | |||
| 100℃，70 hr | -34 | % | |
| The rate of change in hardness of a hardness tester in the air | |||
| 100℃，70 hr | 3.0 | ||
| The rate of change in tensile strength | |||
| 100 ℃, 70 hr, in ASTM # 1 oil | 7.0 | % | |
| 100 ℃, 70 hr, in IRM 903 oil | 8.0 | % | |
| Change rate of ultimate elongation | |||
| 100 ℃, 70 hr, in ASTM # 1 oil | -38 | % | |
| 100 ℃, 70 hr, in IRM 903 oil | -29 | % | |
| The rate of change in Shore hardness | |||
| Support A, 100 ℃, 70 hr, in ASTM # 1 oil | 12 | ||
| Support A, 100 ℃, 70 hr, in IRM 903 oil | 4.0 | ||
| Volume change | |||
| 100 ℃, 70 hr, ASTM standard oil (No.1) | -13 | % | |
| 100 ℃, 70 hr, in IRM 903 oil | -2.0 | % |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Heat loss | 0.40 | % | ASTM D5688 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Ozone resistance | |||
| 50 pphm X 40℃ X 20%，24℃ | no crack |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. at 24 hrs, 48 hrs, 72 hrs, 96 hrs, 168 hrs |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |