| About |
|---|
| NatureFlex™ NVS 120 is a Regenerated Cellulose product. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Applications of NatureFlex™ NVS 120 include bags/liners, film and packaging. Characteristics include: Eco-Friendly/Green Chemical Resistant Clarity Good Sealability Good Stiffness&& |
| Product Description | |
|---|---|
| Generic | 再生纤维 |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good Clarity,Good surface appearance,Good heat sealing,High elastic,Renewable resources,Good Printability,Retention of aroma ,Low to No Fogging,Low odor,Biodegradable,Compostable,Semipermeability,Grease resistance,Antistatic property |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| MECHANICAL | Nominal value | Unit | Test method |
| friction coefficient | ASTM D1894 | ||
| With oneself – dynamic | 0.25 | ASTM D1894 | |
| With oneself – static | 0.25 | ASTM D1894 | |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| Secant modulus | ASTM D882 | ||
| 1% secant, MD: 30 µ m | > 3000 | MPa | ASTM D882 |
| 1% secant, TD: 30 µ m | > 1520 | MPa | ASTM D882 |
| tensile strength | ASTM D882 | ||
| MD, yield, 30 µ m | 124 | MPa | ASTM D882 |
| TD, yield, 30 µ m | 68.9 | MPa | ASTM D882 |
| Tensile strain | ASTM D882 | ||
| MD, fracture, 30 µ m | 22 | % | ASTM D882 |
| TD, fracture, 30 µ m | 70 | % | ASTM D882 |
| Sealing emphasis | 0.12 | N/mm | Internal Method |
| Initial sealing temperature | |||
| 30 µm | 90.6 to 199 | ℃ | Internal Method |
| Oxygen permeability (wet) (24 ℃, 30 µ m, 0.0% RH) | 3.10 | cm³/m²/24 hr | ASTM F1927 |
| Water vapor permeability | 370 | g/m²/24 hr | ASTM E96 |
| film thickness | 30.0 | µm | Internal Method |
| dosage | |||
| 30.0 µm | 23.3 | m²/kg | Internal Method |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 45°，30 µm | 110 | ASTM D2457 | |
| Haze | |||
| 30 µm | 4.0 | % | ASTM D1003 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Thickness: 1.18 mil |
| 3. 275°F, 0.5 secs, 10 psi, thickness: 1.18 mil |
| 4. 100°F, 90%RH, thickness: 1.18 mil |
| 5. 2.5° wide angle |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |