| About |
|---|
| NEALID XG370 is a glass fibre reinforced polyamide alloy intended for Injection moulding. APPLICATIONS NEALID XG370 has been developed especially for very demanding applications in automotive industry and electrical parts. Products requiring excellent combination between thermal and mechanical properties. NEALID XG370 is available in both natural (NEALID XG370) and black (NEALID XG370-8229) but other colours can be provided on request.&& |
| Product Description | |
|---|---|
| Generic | PA + Olefins |
| Material Status | Commercial: Active |
| Features | Renewable resources,HB |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.33 | g/cm³ | ISO 1183 |
| Shrinkage rate | 0.30 to 0.70 | % | |
| Water absorption rate | |||
| Equilibrium, 23 ℃, 50% RH | 0.90 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 10100 | MPa | ISO 527-2 |
| tensile strength | |||
| fracture | 132 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | 2.0 | % | ISO 527-2 |
| Bending modulus | 8900 | MPa | ISO 178 |
| bending strength | 199 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | 12 | kJ/m² | ISO 179 |
| Charpy Unnotch Impact strength | 38 | kJ/m² | ISO 179 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 230 | ℃ | ISO 75-2/A |
| 0.45 MPa, unannealed | 246 | ℃ | ISO 75-2/B |
| Melting temperature | |||
| DSC | 220 | ℃ | ISO 3146 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+15 | ohms | DIN 53482 |
| Volume resistivity | 1.0E+15 | ohms·cm | DIN 53482 |
| Compared to the leakage tracing index | |||
| Solution A | 600 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 1.60 mm | HB | UL 94 | |
| Glowing wire flammability index | |||
| 2.0 mm | 650 | ℃ | IEC 60695-2-12 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 90 | °C | |
| Drying time | 4.0 | hr | |
| Barrel rear temperature | 245 to 270 | °C | |
| Barrel middle temperature | 250 to 280 | °C | |
| Barrel front temperature | 245 to 270 | °C | |
| Nozzle temperature | 245 to 275 | °C | |
| Mold temperature | 60 to 100 | °C | |
| Injection pressure | 85.0 to 110 | MPa | |
| Injection speed | Fast | ||
| Hold pressure | 50.0 to 70.0 | MPa | |
| Screw length to diameter ratio | 15.0:1.0 to 20.0:1.0 | ||
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |