| Product obtained by gas-phase copolymerization of ethylene, butene-1 and hexane-1 in presence of complex metalorganic catalysts. Stabilization recipe: antacid, antioxydant, heat stabilizer, slip additive, antiblocking additive, processing additive, dispersant. Application: high-strength tubular film, improved processability and quality of films surfaces&& |
| Product Description | |
|---|---|
| Generic | Linear low density polyethylene |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Excellent Processability,Good surface appearance,Smoothness,High anti-blocking,Machinable,Acidproof,Inoxidizability,Heat Stabilized |
| Availabilitys | Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.918 to 0.922 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 0.70 to 1.3 | g/10min | ASTM D1238 |
| Gel content | |||
| > 200.0 µm | 250 | pcs/m² | |
| 200.0 to 500.0 µ m | 245 | pcs/m² | |
| 500.0 to 1000.0 µ m | 5.00 | pcs/m² | |
| > 1.00 mm | 0.00 | pcs/m² | |
| Melt flow ratio | |||
| MFR 21.6 kg/MFR 2.16 kg | < 30.0 | ASTM D1238 | |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| Secant modulus | ASTM D882 | ||
| 2% secant, MD | 130 | MPa | ASTM D882 |
| 2% secant, TD | 140 | MPa | ASTM D882 |
| tensile strength | ASTM D882 | ||
| MD, yield | 50.0 | MPa | ASTM D882 |
| TD, yield | 35.0 | MPa | ASTM D882 |
| Tensile strain | ASTM D882 | ||
| MD, fracture | 700 | % | ASTM D882 |
| TD, fracture | 950 | % | ASTM D882 |
| Drop hammer impact | 210 | g | ASTM D1709 |
| Elmandorf tear strength | ASTM D1922 | ||
| MD | 240 | g | ASTM D1922 |
| TD | 480 | g | ASTM D1922 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |