| About |
|---|
| Product obtained by polymerization of propylene in presence of complex metalorganic catalysts. It incorporates enhanced long-term thermal stability, thermal-oxidative degradation resistance at PP production, processing and use of PP-made articles, high resistance to fading from environmental exposure, improved melt rheology. Application: diapers, medical and sanitary fabrics, furniture coating and upholstery.&& |
| Product Description | |
|---|---|
| Generic | PP homopolymerization |
| Material Status | Commercial: Active |
| Features | Controllable rheological,Good color stability,Inoxidizability,Heat Stabilized,Homopolymer |
| Availabilitys | Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.900 | g/cm³ | |
| Apparent density | 0.48 to 0.52 | g/cm³ | |
| Melt Flow Rate | |||
| 230℃，2.16kg | 20 to 30 | g/10min | ASTM D1238 |
| Ash Content | 0.025 to 0.050 | % | |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 150 to 154 | ℃ |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Thermal Creep Temperature | 90 to 96 | ℃ | |
| Thermal oxidation deterioration | |||
| 150℃ | 6.3 | day |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 82 to 95 | ||
| Bending modulus | 1300 | MPa | ASTM D790 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Loading 1 (10 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |