NEFTEKHIM PP 1520J (T38F)

About
Product obtained by polymerization of propylene in presence of complex metalorganic catalysts. It incorporates increased long-term thermal stability, thermal-oxidative degradation resistance during PP production, processing and use of PP-made articles. Application: biaxially oriented film

Product Description
Generic	PP homopolymerization
Material Status	Commercial: Active
Features	Inoxidizability,Homopolymer
Availabilitys	Europe

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.900	g/cm³
Apparent density	0.48 to 0.60	g/cm³
Melt Flow Rate
230℃，2.16kg	2.9 to 3.2	g/10min	ASTM D1238
Ash Content	0.025 to 0.050	%
Gel content
> 200.0 µm	< 300	pcs/m²
0.700 to 1.50 mm	< 3.00	pcs/m²
1.50 to 2.50 mm	0.00	pcs/m²
> 2.50 mm	0.00	pcs/m²

Aging performance	Nominal value	Unit	Test method
Aging resistance
150℃	500	hr

THERMAL	Nominal value	Unit
Hot deformation temperature
0.45 MPa, unannealed	90.0 to 96.0	℃
Vicat Softening Temp	150 to 154	℃

MECHANICAL	Nominal value	Unit	Test method
Rockwell hardness
R-level	82 to 95
tensile strength
yield	> 34.0	MPa	ASTM D638
Tensile strain
yield	> 10	%	ASTM D638
Bending modulus	> 1450	MPa	ASTM D790

Notes
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.