| About |
|---|
| Product obtained by copolymerization of propylene and ethylene in presence of complex metalorganic catalysts. It incorporates increased long-term thermal stability, thermal-oxidative degradation resistance during PP production, processing and use of PP-made articles. Application: compounding, injection molding&& |
| Product Description | |
|---|---|
| Generic | PP copolymer |
| Material Status | Commercial: Active |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.900 | g/cm³ | |
| Apparent density | 0.48 to 0.60 | g/cm³ | |
| Melt Flow Rate | |||
| 230℃，2.16kg | 15 to 25 | g/10min | ASTM D1238 |
| Ash Content | 0.025 to 0.050 | % | |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | ASTM D256 | ||
| -20℃ | 35 | J/m | |
| 23℃ | 70 | J/m |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 126 to 150 | ℃ |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Thermal Creep Temperature | 64 to 90 | ℃ | |
| Thermal oxidation deterioration | |||
| 150℃ | 15.0 | day |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 40 to 88 | ||
| Bending modulus | 1000 | MPa | ASTM D790 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Loading 1 (10 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |