| About |
|---|
| Neoflon® PFA AP-210 is a medium melt flow PFA resin suitable for injection molding and for electrical wire coatings. Typical Applications: Tubing, wire insulation and injection molded parts.&& |
| Product Description | |
|---|---|
| Supplier | Daikin Fluorochemicals |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Flame Characteristics,Corrosion Resistant,Copolymer,Low coefficient of friction,Good Rigidity,Good Electrical Properties,V-0,Good liquidity,Excellent Processability,Good Clarity |
| Availabilitys | Asia Pacific,North America |
| Process Methods | Injection Molding,Extrusion |
| Technical Data | |||
|---|---|---|---|
| IMPACT | Nominal value | Unit | Test method |
| Impact strength of cantilever beam notch | 无断裂 | ASTM D256 | |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting temperature | 300 to 310 | ℃ | ASTM D4591 |
| Linear coefficient of thermal expansion | |||
| MD：20~100℃ | 1.2E-4 | 1/℃ | ASTM D696 |
| specific heat | 1050 | J/kg/℃ | |
| Thermal conductivity coefficient | 0.26 | W/m/K | ASTM C177 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 1.60 mm | V-0 | UL 94 | |
| Extreme oxygen index | |||
| 1.57 mm | > 95 | % | ASTM D2863 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 60 to 70 | ASTM D2240 | |
| tensile strength | |||
| yield | 25.4 to 30.4 | MPa | JIS K6891 |
| Tensile strain | |||
| fracture | 350 to 450 | % | JIS K6891 |
| Bending modulus | 580 to 690 | MPa | ASTM D790 |
| Compression modulus | 490 to 590 | MPa | ASTM D695 |
| compressive strength | ASTM D695 | ||
| 1% strain | 4.90 to 5.90 | MPa | ASTM D695 |
| 25% strain | 31.4 to 33.3 | MPa | ASTM D695 |
| friction coefficient | |||
| Steel – Static | 0.040 to 0.050 | ||
| Load deformation | ASTM D621 | ||
| 25℃，14 MPa | 2.50 to 3.00 | % | ASTM D621 |
| 25℃，14 MPa | 8.00 to 9.00 | % | ASTM D621 |
| 100℃，6.9 MPa | 2.00 to 3.00 | % | ASTM D621 |
| 100℃，6.9 MPa | 8.50 to 9.50 | % | ASTM D621 |
| bending strength | No break | ASTM D790 |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | 2.14 to 2.16 | g/cm³ | ASTM D792 |
| Apparent density | 1.00 to 1.40 | g/cm³ | JIS K6891 |
| Melt Flow Rate | |||
| 372℃，5.0kg | 10 to 17 | g/10min | ASTM D1238 |
| Water absorption rate | |||
| saturated | < 0.010 | % | ASTM D570 |
| Apparent viscosity of melt | |||
| 380℃ | 2.00E+6 to 2.50E+7 | mPa·s |
| Process Conditions | |||
|---|---|---|---|
| Injection Molding | Nominal value | Unit | Test method |
| Rear Temperature -Zone 1 | 350-360 | ℃ | |
| Middle Temperature -Zone 2 | 370-390 | ℃ | |
| Front Temperature -Zone 3 | 380-400 | ℃ | |
| Injection port temperature | 380-400 | ℃ | |
| Mold Temperature | 200 | ℃ | |
| Screw Speed | 180 | rpm | |
| Injection pressure | 29.4-68.6 | MPa | |
| Hold Pressure | 44.1 | MPa | |
| Hold Time | 20 | s | |
| injection velocity | 0.95 | ||
| Cooling time | 60 | s | |
| forming time | 120 | s/cycle | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. DSC |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |