NEOFLON™ EFEP RP-4040

About
EFEP RP-4020 and RP-4040 are fluoropolymers combining the excellent physical and chemical properties derived from ETFE together with the very low melting temperature characteristic of a conventional thermoplastic. These resins have a high transparency and adhere well to many kinds of plastics and inorganic materials (glass, metals) without adhesive or etching. EFEP RP-4020 and RP-4040 offer the following advantages for a wide range of applications found in the chemical processing, semiconductor and film industries: Very low processing temperature and excellent thermal stability High transparency Excellent chemical resistance High purity Excellent weathering Improved heat sealing properties Low mold shrinkage (injection molding) Co-extrusion with other resins (nylons, EVOH, modified PE, and ETFE) without adhesive or etching&&

About

EFEP RP-4020 and RP-4040 are fluoropolymers combining the excellent physical and chemical properties derived from ETFE together with the very low melting temperature characteristic of a conventional thermoplastic. These resins have a high transparency and adhere well to many kinds of plastics and inorganic materials (glass, metals) without adhesive or etching. EFEP RP-4020 and RP-4040 offer the following advantages for a wide range of applications found in the chemical processing, semiconductor and film industries: Very low processing temperature and excellent thermal stability High transparency Excellent chemical resistance High purity Excellent weathering Improved heat sealing properties Low mold shrinkage (injection molding) Co-extrusion with other resins (nylons, EVOH, modified PE, and ETFE) without adhesive or etching&&

Product Description
Supplier	Daikin Fluorochemicals
Generic	含氟聚合物
Material Status	Commercial: Active
Features	Weather resistance is good,Good Clarity,High purity,Good heat sealing,Low contractility,Good bond,Solvent resistance,Heat Stabilized
Availabilitys	North America

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.74	g/cm³	ASTM D792
Melt Flow Rate
265℃，5.0kg	3.0 to 8.0	g/10min	ASTM D1238

MECHANICAL	Nominal value	Unit	Test method
tensile strength
yield	55.0	MPa	ASTM D638
Tensile strain
fracture	450	%	ASTM D638

THERMAL	Nominal value	Unit	Test method
Melting temperature	160	℃	DSC

Process Conditions
Extrusion	Nominal value	Unit	Test method
Barrel 1 zone temperature	170	°C
Barrel 2 zone temperature	185	°C
Barrel 3 zone temperature	210	°C
Barrel 4 zone temperature	220	°C
Connector temperature	225	°C
Nozzle temperature	210	°C

Notes
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.