| Eastman Neostar™ Elastomer FN005 is a tough, clear, durable, general purpose grade copolyester ether. It was designed for use in the profile and automotive markets, but is also used in packaging and tubing applications where toughness and flex-crack resistance are required. Eastman Neostar™ Elastomer FN005 can be used in injection molding and cast film or tubing extrusion applications or in any application that demands strength, durability, and puncture resistance in harsh environments. This copolyester combines toughness, clarity, and flexibility without the addition of plasticizers. Eastman Neostar™ Elastomer FN005 is considered environmentally preferred because of its non-halogenated material composition. The target inherent viscosity of this product is 1.05. This product has been CRADLE TO CRADLE CERTIFIED Silver. The CRADLE TO CRADLE CERTIFIED Mark is a registered certification mark used under license through McDonough Braungart Design Chemistry (MBDC). MBDC is a global sustainability consulting and product certification firm. The CRADLE TO CRADLE® framework moves beyond the traditional goal of reducing the negative impacts of commerce (‘eco-efficiency’), to a new paradigm of increasing its positive impacts (‘eco-effectiveness’). At its core, Cradle to Cradle design perceives the safe and productive processes of nature’s ‘biological metabolism’ as a model for developing a ‘technical metabolism’ flow of industrial materials. Product components can be designed for continuous recovery and reutilization as biological and technical nutrients within these metabolisms. For more information about MBDC and to obtain printable certificates for Eastman Copolyesters, visit www.mbdc.com. Choose Eastman Chemical Company under Company Name in C2C Certified products to display a list of our products.&& |
| Product Description | |
|---|---|
| Supplier | Eastman |
| Generic | 共聚酯醚弹性体 |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good Clarity,Good flexibility,Good Dimensional Stability,Halogen free,High Heat Resistance,Good tear strength,Durability,Solvent resistance,Puncture Resistant |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.13 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 20 | g/10min | ASTM D1238 |
| Water absorption rate | |||
| 23℃，24hr | 0.35 | % | ASTM D570 |
| Intrinsic viscosity | |||
| 23℃ | 1.1 | Internal Method | |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 130 | µm | |
| Secant modulus | ASTM D882 | ||
| Tangent, MD: 130 µ m | 185 | MPa | ASTM D882 |
| Tangent, TD: 130 µ m | 179 | MPa | ASTM D882 |
| tensile strength | ASTM D882 | ||
| MD, yield, 130 µ m | 13.7 | MPa | ASTM D882 |
| TD, yield, 130 µ m | 13.5 | MPa | ASTM D882 |
| MD, fracture, 130 µ m | 23.7 | MPa | ASTM D882 |
| TD, fracture, 130 µ m | 22.6 | MPa | ASTM D882 |
| Tensile strain | ASTM D882 | ||
| MD, yield, 130 µ m | 26 | % | ASTM D882 |
| TD, yield, 130 µ m | 26 | % | ASTM D882 |
| MD, fracture, 130 µ m | 550 | % | ASTM D882 |
| TD, fracture, 130 µ m | 550 | % | ASTM D882 |
| Oxygen permeability | |||
| 30℃，130 µm | 841 | cm³/m²/24 hr | ASTM D1434 |
| Water vapor permeability | 130 | g/m²/24 hr | ASTM F372 |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| Kappa’s modulus | ASTM D1043 | ||
| -70℃ | 930 | MPa | ASTM D1043 |
| -28℃ | 240 | MPa | ASTM D1043 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| -40℃ | 50 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Embrittlement temperature | < -75.0 | ℃ | ASTM D746 |
| Glass transition temperature | -3.00 | ℃ | DSC |
| Vicat Softening Temp | 170 | ℃ | ASTM D1525 6 |
| Melting peak temperature | 207 | ℃ | ASTM D3418 |
| Crystallization peak temperature | |||
| DSC | 140 | ℃ | DSC |
| Linear coefficient of thermal expansion | |||
| MD：23℃ | 1.5E-4 | 1/℃ | ASTM D696 |
| specific heat | DSC | ||
| 25℃ | 1600 | J/kg/℃ | DSC |
| 100℃ | 1800 | J/kg/℃ | DSC |
| 150℃ | 2000 | J/kg/℃ | DSC |
| 175℃ | 2300 | J/kg/℃ | DSC |
| 200℃ | 3100 | J/kg/℃ | DSC |
| 225℃ | 2300 | J/kg/℃ | DSC |
| Thermal conductivity coefficient | |||
| 23℃ | 0.19 | W/m/K | ASTM C177 |
| Fusion heat | |||
| 23℃ | 27.0 | kJ/kg | ASTM E793 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| tear strength | |||
| 23℃ | 370 | N | ASTM D1004 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | ASTM D2240 | ||
| Shore A, 23 ℃ | 95 | ASTM D2240 | |
| Shore D, 23 ℃ | 55 | ASTM D2240 | |
| Tensile modulus | |||
| 23℃ | 170 | MPa | ASTM D638 |
| tensile strength | ASTM D638 | ||
| Yield, 23 ℃, 3 mm, injection molding | 14.0 | MPa | ASTM D638 |
| Fracture, 23 ℃, 2 mm | 20.0 | MPa | ASTM D638 |
| Tensile strain | ASTM D638 | ||
| Yield, 23 ℃ | 30 | % | ASTM D638 |
| Fracture, 23 ℃ | 300 | % | ASTM D638 |
| Bending modulus | |||
| 23℃ | 150 | MPa | ASTM D790 |
| friction coefficient | > 1.0 | ASTM D1894 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. EMN-A-AC-G-V-1 |
| 3. Type I, 20 in/min |
| 4. Type IV, 20 in/min |
| 5. 0.13 mm |
| 6. Loading 1 (10 N) |
| 7. Solid |
| 8. Transition, apparent specific heat, including the effects of the heat of fusion. |
| 9. Melt |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |