| Product Description: Nex-Pro TPO5150D is a flexible TPE/TPO hybrid intended for injection molding applications, offering good processibility, easy coloring, good heat resistance, improved flexural fatigue and impact resistance. Features: Easy to process Very good impact resistance Good ozone resistance Good UV resistance Ease of coloring by proper masterbatch&& |
| Product Description | |
|---|---|
| Generic | Polyolefin Elastomer |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Excellent Processability,Good flexibility,High impact resistance,Fatigue resistance,Ozone resistance,Heat Resistance, Good,Good coloring |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.920 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 21 | g/10min | ASTM D1238 |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tear strength | 78.8 | kN/m | ASTM D624 |
| Compression deformation | |||
| 23℃，22 hr | 54 | % | |
| 70℃，22 hr | 75 | % |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Embrittlement temperature | -50.0 | ℃ | ASTM D746 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shore A, 10 seconds, extrusion molding | 96 | ||
| Shore A, 10 seconds, injection molding | 97 | ||
| Shore D, 10 seconds, extrusion molding | 48 | ||
| Shore D, 10 seconds, injection molding | 50 | ||
| Tensile modulus | |||
| 100% secant | 4.96 | MPa | ASTM D638 |
| tensile strength | |||
| fracture | 14.4 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 350 | % | ASTM D638 |
| Bending modulus | |||
| tangent | 386 | MPa | ASTM D790 |
| bending strength | 14.2 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Squeeze description | Nominal value | Unit | Test method |
| Extrusion | Nominal value | Unit | Test method |
| Drying temperature | 66 to 71 | °C | |
| Drying time | 2.0 to 3.0 | hr | |
| Barrel rear temperature | 170 to 200 | °C | |
| Barrel middle temperature | 180 to 210 | °C | |
| Barrel front temperature | 190 to 220 | °C | |
| Nozzle temperature | 200 to 230 | °C | |
| Processing (melt) temperature | 200 to 220 | °C | |
| Mold temperature | 10 to 50 | °C | |
| Screw speed | 50 to 200 | rpm | |
| Drying temperature | 66 to 71 | °C | |
| Drying time | 2.0 to 3.0 | hr | |
| Barrel 1 zone temperature | 160 to 180 | °C | |
| Barrel 2 zone temperature | 170 to 190 | °C | |
| Barrel 3 zone temperature | 180 to 200 | °C | |
| Barrel 4 zone temperature | 190 to 210 | °C | |
| Melt temperature | 190 to 200 | °C | |
| Nozzle temperature | 190 to 210 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. (break) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |