| About |
|---|
| Description ABS Un Filled Black Compound Product Applications Typical application such as computer monitor,Printer,Photocopying machine,calculators ,Battries,Lighting diffusers, Auto exterior parts etc Benefits Good low Temperature Toughness, High gloss & weather resistance&& |
| Product Description | |
|---|---|
| Generic | ABS |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Good surface appearance,Antifreeze,HB |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.04 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 220℃，5.0kg | 15 | g/10min | ASTM D1238 |
| Shrinkage rate | ASTM D955 | ||
| MD | 0.60 | % | ASTM D955 |
| TD | 0.60 | % | ASTM D955 |
| Water absorption rate | ASTM D570 | ||
| 23℃，24hr | 0.30 | % | ASTM D570 |
| saturated | 0.70 | % | ASTM D570 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 160 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 0.45 MPa, unannealed | 110 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 95.0 | ℃ | ASTM D648 |
| Vicat Softening Temp | 105 | ℃ | ASTM D1525 |
| Relative temperature index | |||
| Electrical performance | 60.0 | ℃ | UL 746 |
| Impact mechanical performance | 60.0 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Dielectric strength | 18 | kV/mm | ASTM D149 |
| Arc resistance | 160 | sec | ASTM D495 |
| Arc resistance | PLC 5 | ASTM D495 | |
| Compared to the leakage tracing index | > 550 | V | UL 746 |
| Compared to the leakage tracing index | PLC 0 | UL 746 | |
| Hot wire ignition | |||
| HWI | PLC 3 | UL 746 | |
| HWI | 22 | sec | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 0.80 mm | HB | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 95 | ASTM D785 | |
| Tensile modulus | 2000 | MPa | ASTM D638 |
| tensile strength | 40.0 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 17 | % | ASTM D638 |
| Bending modulus | 2100 | MPa | ASTM D790 |
| bending strength | 72.0 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature – vacuum dryer | 70 | °C | |
| Drying time | 4.0 to 6.0 | hr | |
| Recommended maximum moisture content | 0.20 | % | |
| Barrel rear temperature | 210 to 220 | °C | |
| Barrel middle temperature | 220 to 230 | °C | |
| Barrel front temperature | 230 to 240 | °C | |
| Mold temperature | 45 to 65 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Immersed |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |