| Description Polyphenylene Sulfide Glass Fiber Reinforced Anti wear Black Compound Product Applications This is High performance material & This grade is used for Appliance, Automotive, Electric/Electronics, & industrial Application Benefits Better dimensional stability, wear & abrasion properties, High thermal stability, chemical resistance & flame resistance&& |
| Product Description | |
|---|---|
| Generic | PPS |
| Material Status | Commercial: Active |
| Features | Good Dimensional Stability,Flame Characteristics,Good wear resistance,Solvent resistance,Heat Stabilized,V-0 |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.70 | g/cm³ | ASTM D792 |
| Shrinkage rate | ASTM D955 | ||
| MD | 0.25 | % | ASTM D955 |
| TD | 0.25 | % | ASTM D955 |
| Water absorption rate | ASTM D570 | ||
| 23℃，24hr | 0.040 | % | ASTM D570 |
| saturated | 4.2 | % | ASTM D570 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 88 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 0.45 MPa, unannealed | 275 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 260 | ℃ | ASTM D648 |
| Melting temperature | 280 | ℃ | ASTM D2117 |
| Relative temperature index | |||
| Electrical performance | 240 | ℃ | UL 746 |
| Impact mechanical performance | 220 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+13 | ohms | IEC 60093 |
| Volume resistivity | 1.0E+17 | ohms·cm | IEC 60093 |
| Dielectric strength | 26 | kV/mm | IEC 60243-1 |
| Compared to the leakage tracing index | 225 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 0.80 mm | V-0 | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | ASTM D785 | ||
| M-level | 100 | ASTM D785 | |
| R-level | 110 | ASTM D785 | |
| Tensile modulus | 7800 | MPa | ASTM D638 |
| tensile strength | 100 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 2.0 | % | ASTM D638 |
| Bending modulus | 6800 | MPa | ASTM D790 |
| bending strength | 160 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature – vacuum dryer | 130 | °C | |
| Drying time | 4.0 to 6.0 | hr | |
| Recommended maximum moisture content | 0.10 | % | |
| Barrel rear temperature | 290 to 300 | °C | |
| Barrel middle temperature | 310 to 320 | °C | |
| Barrel front temperature | 310 to 320 | °C | |
| Mold temperature | 130 to 145 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Immersed |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |