NEXUS BIO BIO-100

About
Film Blowing Grade Starch-Based Biodegradable Resin Nexus BIO-100 is a Hybrid starch resin based on the combination of thermoplastic starch (25%-75%), degradable polyethylene (10-45%) and other self oxidation. This grade of resin is designed for manufacturing biodegradable plastic films with high mechanical strength, outstanding elongation properties and toughness and easily colored. Applications include agricultural films, garbage bags (with / without poly drawstring), merchandise bags (T-shirt bags / shopping bag), Promotional bags, Special inside / outside packaging.&&

About

Film Blowing Grade Starch-Based Biodegradable Resin Nexus BIO-100 is a Hybrid starch resin based on the combination of thermoplastic starch (25%-75%), degradable polyethylene (10-45%) and other self oxidation. This grade of resin is designed for manufacturing biodegradable plastic films with high mechanical strength, outstanding elongation properties and toughness and easily colored. Applications include agricultural films, garbage bags (with / without poly drawstring), merchandise bags (T-shirt bags / shopping bag), Promotional bags, Special inside / outside packaging.&&

Product Description
Generic	生物可降解聚合物
Material Status	Commercial: Active
Features	Good Rigidity,Good flexibility,Renewable resources,Biodegradable,Good Tensile Strength,Good coloring
Availabilitys	North America

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.05	g/cm³	Internal Method
Melt Flow Rate	0.80 to 1.5	g/10min	Internal Method
water content	0.50	%	Internal Method

film	Nominal value	Unit	Test method
tensile strength			Internal Method
MD, yield	25.6	MPa	Internal Method
TD, yield	33.0	MPa	Internal Method
Tensile strain			Internal Method
MD, fracture	380	%	Internal Method
TD, fracture	560	%	Internal Method

THERMAL	Nominal value	Unit	Test method
Vicat Softening Temp	> 65.0	℃	Internal Method

Supplementary information	Nominal value	Unit	Test method
Biology Content	> 62	%	Internal Method
Hexane Extraction	< 4.0	%	Internal Method
Starch Content	> 35	%	Internal Method
tear strength
Right Angle	> 40.0	MPa	Internal Method

Process Conditions
Extrusion	Nominal value	Unit	Test method
Barrel 1 zone temperature	175	°C
Barrel 2 zone temperature	180	°C
Barrel 3 zone temperature	185	°C
Barrel 4 zone temperature	180	°C

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.