About
NHU-PPS 1170C NHU-PPS Polymer is featuring narrow molecular weight distribution, low content of oligomer and stable properties. By adopting advanced automated polymerization and post-processing technology, NHU are nmnufacturing PPS of different grades with MFR ranging from 50-3000. In the nmanwhile, NHU can provide various specifications encompassing linear, cross-linked and other grades.&&NHU-PPS 1170C NHU-PPS Polymer is featuring narrow molecular weight distribution, low content of oligomer and stable properties. By adopting advanced automated polymerization and post-processing technology, NHU are nmnufacturing PPS of different grades with MFR ranging from 50-3000. In the nmanwhile, NHU can provide various specifications encompassing linear, cross-linked and other grades.&&

About

NHU-PPS 1170C NHU-PPS Polymer is featuring narrow molecular weight distribution, low content of oligomer and stable properties. By adopting advanced automated polymerization and post-processing technology, NHU are nmnufacturing PPS of different grades with MFR ranging from 50-3000. In the nmanwhile, NHU can provide various specifications encompassing linear, cross-linked and other grades.&&NHU-PPS 1170C NHU-PPS Polymer is featuring narrow molecular weight distribution, low content of oligomer and stable properties. By adopting advanced automated polymerization and post-processing technology, NHU are nmnufacturing PPS of different grades with MFR ranging from 50-3000. In the nmanwhile, NHU can provide various specifications encompassing linear, cross-linked and other grades.&&

Product Description
Supplier	NHU
Generic	PPS
Material Status	Commercial: Active
Features	Weight distribution
Availabilitys	Asia Pacific
Process Methods	Injection Molding

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Melt Flow Rate
316℃，5.0kg	750	g/10min	ISO 1133
Ash Content
750℃	0.4	%	ISO 3451

Supplementary information	Nominal value	Unit	Test method
Heating reduction	0.10	%
volatility	0.40	%

Process Conditions
injection	Nominal value	Unit	Test method
Drying temperature	165	°C
Drying time	2.0 to 3.0	hr
Barrel rear temperature	300 to 315	°C
Barrel middle temperature	310 to 330	°C
Barrel front temperature	315 to 330	°C
Nozzle temperature	300 to 315	°C
Mold temperature	130 to 150	°C
Back pressure	4.00 to 5.00	MPa

Notes
1. Typical properties: these are not to be construed as specifications.
2. 300°C, 1 hour
3. 150°C, 1 hour
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.