| Nofia® CO3000 is a poly(phosphonate-co-carbonate) and is part of a family of products that can be produced in a range of compositions from high to low phosphonate content. The copolymers have good impact resistance and glass transition temperatures while maintaining high melt flow and a high limiting oxygen index.&& |
| Product Description | |
|---|---|
| Generic | PPh+PC |
| Material Status | Commercial: Active |
| Features | Good Clarity,High liquidity,Copolymer |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Melt Volume Rate | |||
| 240℃，2.16 kg | 7.00 | cm³/10min | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 2800 | MPa | |
| tensile strength | |||
| yield | 65.0 | MPa | |
| fracture | 53.0 | MPa | |
| Tensile strain | |||
| yield | 5.0 | % | |
| fracture | 110 | % | |
| Bending modulus | 2800 | MPa | |
| bending strength | |||
| yield | 110 | MPa |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃，2mm | 500 | J/m | |
| Impact strength of cantilever beam notch | |||
| 23℃ | 无断裂 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 125 | ℃ | |
| 1.8 MPa, unannealed | 115 | ℃ |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 0.40 mm | V-0 | UL 94 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Transmittance | > 88.0 | % |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Hydrolysis stability | |||
| No Change in Mw，90℃ | 4.2 | day |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature – hot air dryer | 100 | °C | |
| Drying time – hot air dryer | 4.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Barrel rear temperature | 230 | °C | |
| Barrel middle temperature | 235 | °C | |
| Barrel front temperature | 240 | °C | |
| Nozzle temperature | 240 | °C | |
| Mold temperature | 65 | °C | |
| Back pressure | 0.200 to 0.250 | MPa | |
| Screw speed | 100 | rpm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 5% Strain |
| 3. 90% RH |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |