| KE901 is Outstanding impact strength and Excellent clarity PEN-PET copolyester Grade.&& |
| Product Description | |
|---|---|
| Supplier | Kolon |
| Generic | PEN |
| Material Status | Commercial: Active |
| Features | V-2 |
| Availabilitys | North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.34 | g/cm³ | ASTM D792 |
| Density | 1.34 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 275℃，2.16kg | 12 | g/10min | ISO 1133 |
| Shrinkage rate | 0.60 | % | ISO 294-4 |
| Water absorption rate | |||
| 23℃，24hr | 0.10 | % | ISO 62 |
| Intrinsic viscosity | 0.84 | dl/g | Internal Method |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 3.0 | kJ/m² | ISO 179/1eA |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 100 | ℃ | ASTM D648-A |
| 0.45 MPa, unannealed | 115 | ℃ | ISO 75-2/B |
| Vicat Softening Temp | 280 | ℃ | ASTM D1525 |
| Melting temperature | 265 | ℃ | ISO 11357-3 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 0.80 mm | V-2 | UL 94 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Transmittance | |||
| total | 85.0 | % | ASTM D1003 |
| Haze | 2.0 | % | ASTM D1003 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| Yield, 23 ℃ | 64.0 | MPa | ISO 527-2 |
| 23℃ | 63.0 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 23 ℃ | 6.4 | % | ASTM D638 |
| Fracture, 23 ℃ | 6.4 | % | ISO 527-2 |
| Bending modulus | |||
| 23℃ | 2900 | MPa | ISO 178 |
| 23℃ | 2890 | MPa | ASTM D790 |
| Rockwell hardness | 110 | ISO 2039-2 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature – hot air dryer | 140 to 160 | °C | |
| Drying time – hot air dryer | 3.0 to 6.0 | hr | |
| Recommended maximum moisture content | < 0.080 | % | |
| Barrel rear temperature | 200 to 240 | °C | |
| Barrel middle temperature | 250 to 270 | °C | |
| Barrel front temperature | 250 to 280 | °C | |
| Nozzle temperature | 260 to 290 | °C | |
| Mold temperature | 30 to 80 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |