| About |
|---|
| Extrusion grade. 254F (123C) DTUL. UL94 V-1 rated.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PPO(PPE)+PS |
| Material Status | Commercial: Active |
| Features | V-1,V-0 |
| Availabilitys | North America |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.08 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.50 to 0.70 | % | Internal Method |
| Water absorption rate | |||
| 24hr | 0.070 | % | ASTM D570 |
| Weathering resistance | f1 | UL 746C | |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | ASTM D256 | ||
| -40℃ | 130 | J/m | ASTM D256 |
| 23℃ | 190 | J/m | ASTM D256 |
| Drop hammer impact | ASTM D3029 | ||
| -40℃ | 4.07 | J | ASTM D3029 |
| -30℃ | 14.9 | J | ASTM D3029 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 6.4 mm | 123 | ℃ | ASTM D648 |
| Linear coefficient of thermal expansion | |||
| MD：-40~95℃ | 5.9E-5 | 1/℃ | ASTM E831 |
| Relative temperature index | |||
| Electrical performance | 110 | ℃ | UL 746 |
| Strength mechanical performance | 110 | ℃ | UL 746 |
| Impact mechanical performance | 105 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Dielectric strength | |||
| 3.2 mm in oil | 20 | kV/mm | ASTM D149 |
| Dielectric constant | ASTM D150 | ||
| 50 Hz | 2.69 | ASTM D150 | |
| 60 Hz | 2.69 | ASTM D150 | |
| Dissipation factor | ASTM D150 | ||
| 50 Hz | 7.0E-4 | ASTM D150 | |
| 60 Hz | 7.0E-4 | ASTM D150 | |
| Arc resistance | PLC 6 | ASTM D495 | |
| Compared to the leakage tracing index | PLC 1 | UL 746 | |
| High voltage arc marking rate | |||
| HVTR | PLC 4 | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 1.50 mm | V-1 | UL 94 | |
| 6.00 mm | V-0 | UL 94 | |
| Extreme oxygen index | 29 | % | ASTM D2863 |
| Radiation Plate Listing (UL) | RP100 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| yield | 63.4 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 25 | % | ASTM D638 |
| Bending modulus | |||
| 100 mm span | 2550 | MPa | ASTM D790 |
| bending strength | |||
| Yield, 100 mm span | 99.3 | MPa | ASTM D790 |
| Rockwell hardness | |||
| R-level | 119 | ASTM D785 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Drying temperature | 104 to 116 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Barrel 1 zone temperature | 204 | °C | |
| Barrel 2 zone temperature | 204 | °C | |
| Barrel 3 zone temperature | 227 | °C | |
| Barrel 4 zone temperature | 227 | °C | |
| Connector temperature | 249 | °C | |
| Melt temperature | 227 to 254 | °C | |
| Nozzle temperature | 249 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Type I, 2.0 in/min |
| 3. 0.10 in/min |
| 4. Tungsten Electrode |
| 5. UL Tested |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |