| Noryl* FE1410PW resin is a blend of polyphenylene Oxide (PPO) and polystyrene (PS) resin that contains 10% glass reinforcement. The resin is suitable for injection molding. Noryl FE1410PW resin has been developed for fluid engineering applications that require improved hydrolytic stability. Noryl FE1410PW resin has been certified for potable water applications up to 85C in Europe and North America in limited colors.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PPO(PPE)+PS |
| Material Status | Commercial: Active |
| Features | Hydrolysis stability |
| Availabilitys | North America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.13 | g/cm³ | ISO 1183 |
| Melt Volume Rate | |||
| 280℃，10 kg | 32.0 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.20 to 0.40 | % | Internal Method |
| Water absorption rate | |||
| Saturation, 23 ℃ | 0.20 | % | ISO 62 |
| Balance, 50% RH | 0.060 | % | ASTM D570 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 4780 | MPa | ASTM D638 |
| Tensile modulus | 4930 | MPa | ISO 527-1-2 |
| tensile strength | |||
| fracture | 94.0 | MPa | ISO 527-2/5 |
| fracture | 94.0 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 2.7 | % | ISO 527-2/5 |
| fracture | 2.8 | % | ASTM D638 |
| Bending modulus | 4880 | MPa | ISO 178 |
| 50 mm span | 4860 | MPa | ASTM D790 |
| bending strength | 135 | MPa | ISO 178 |
| bending strength | |||
| Fracture, 50 mm span | 135 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 3.0 | kJ/m² | ISO 179/2C |
| Charpy Unnotch Impact strength | ISO 179/1eU | ||
| -30℃ | 14 | kJ/m² | ISO 179/1eU |
| 23℃ | 14 | kJ/m² | ISO 179/1eU |
| Impact strength of cantilever beam notch | ASTM D256 | ||
| -30℃ | 35 | J/m | ASTM D256 |
| 23℃ | 35 | J/m | ASTM D256 |
| Impact strength of cantilever beam notch | ISO 180/1A | ||
| -30℃ | 4.0 | kJ/m² | ISO 180-1A |
| 23℃ | 4.0 | kJ/m² | ISO 180-1A |
| Impact strength of cantilever beam notch | ASTM D4812 | ||
| -30℃ | 230 | J/m | ASTM D4812 |
| 23℃ | 230 | J/m | ASTM D4812 |
| Notched impact strength of cantilever beam | ISO 180/1U | ||
| -30℃ | 13 | kJ/m² | ISO 180/1U |
| 23℃ | 13 | kJ/m² | ISO 180/1U |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 3.2 mm | 127 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 100 mm span | 126 | ℃ | ISO 75-2/Ae |
| 0.45 MPa, unannealed, 100 mm span | 135 | ℃ | ISO 75-2/Be |
| Vicat Softening Temp | |||
| A50 | 146 | ℃ | ISO 306/A50 |
| B120 | 140 | ℃ | ISO 306/B120 |
| Linear coefficient of thermal expansion | |||
| TD：-40~40℃ | 7.0E-5 | 1/℃ | ISO 11359-2 |
| MD：-40~40℃ | 3.0E-5 | 1/℃ | ISO 11359-2 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 100 to 120 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Hopper temperature | 60 to 80 | °C | |
| Barrel rear temperature | 250 to 270 | °C | |
| Barrel middle temperature | 270 to 290 | °C | |
| Barrel front temperature | 290 to 310 | °C | |
| Nozzle temperature | 280 to 300 | °C | |
| Processing (melt) temperature | 280 to 300 | °C | |
| Mold temperature | 80 to 120 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.20 in/min |
| 3. Type I, 0.20 in/min |
| 4. 0.051 in/min |
| 5. 0.079 in/min |
| 6. at Break |
| 7. 80*10*4 sp=62mm |
| 8. 80*10*4 mm |
| 9. 120*10*4 mm |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |