| Non brominated non chlorinated flame retarded NORYL resin for structural foam applications. 80C HDT. All values at 20% weight reduction.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PPO(PPE)+PS |
| Material Status | Commercial: Active |
| Features | Foaming performance,Halogen free,Flame Characteristics,V-1,V-0,5VA |
| Availabilitys | North America |
| Process Methods | Foam treatment |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | ASTM D792 | ||
| — | 0.878 | g/cm³ | ASTM D792 |
| — | 1.12 | g/cm³ | ASTM D792 |
| Melt Volume Rate | |||
| 280℃，5 kg | 36.0 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| MD：6.4 mm | 0.50 to 0.80 | % | Internal Method |
| Water absorption rate | |||
| 24hr | 0.070 | % | ASTM D570 |
| Foam（Physical） | 20 | % | Internal Method |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | ASTM D638 | ||
| Yield, 6.35 mm | 36.0 | MPa | ASTM D638 |
| Fracture, 6.35 mm | 34.0 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 6.35 mm | 12 | % | ASTM D638 |
| Bending modulus | |||
| 6.40 mm | 2250 | MPa | ASTM D790 |
| bending strength | |||
| Yield, 6.40 mm | 70.0 | MPa | ASTM D790 |
| Foam（Mechanical） | 20 | % | Internal Method |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Notched impact strength of cantilever beam | |||
| 23℃，6.4 mm | 360 | J/m | ASTM D4812 |
| Dart impact equipped with measuring instruments | |||
| 23℃，Energy at Peak Load | 29.0 | J | ASTM D3763 |
| Foam（Impact） | 20 | % | Internal Method |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 0.45 MPa, unannealed, 6.4 mm | 93.0 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 6.4 mm | 82.0 | ℃ | ASTM D648 |
| Relative temperature index | 65.0 | ℃ | UL 746 |
| Electrical performance | 65.0 | ℃ | UL 746 |
| Impact mechanical performance | 65.0 | ℃ | UL 746 |
| Foam（Thermal） | 20 | % | Internal Method |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 3.00 mm | V-1 | UL 94 | |
| 6.00 mm | V-0 | UL 94 | |
| 3.90 mm | 5VA | UL 94 | |
| Foam（Flame Class Minimum Density） | 850 | kg/m³ | Internal Method |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Foam Molded |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |