| About |
|---|
| NORYL FP6130 is an unfilled, injection moldable modified polyphenylene ether resin. Designed for good dimensional stability and high flow , this resin also uses non-chlorinated, non-brominated FR additives to achieve a V1 UL94 rating at 1.5 mm with a specific density of 1.1 g/cm^3. NORYL FP6130 may be an excellent material candidate for Flat Panel TV enclosure applications requiring good rheological properties, heat resistance, hydrolysis resistance, low density and thin wall flame resistance.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PPO(PPE)+PS |
| Material Status | Commercial: Active |
| Features | Good Dimensional Stability,High liquidity,Hydrolysis stability,Halogen free,Flame Characteristics,High Heat Resistance,Low density,V-1 |
| Availabilitys | North America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.10 | g/cm³ | ASTM D792 |
| Density | 1.10 | g/cm³ | ISO 1183 |
| Melt Volume Rate | ISO 1133 | ||
| 300℃，1.2 kg | 15.0 | cm³/10min | ISO 1133 |
| 280℃，2.16 kg | 34.0 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.50 to 0.70 | % | Internal Method |
| Water absorption rate | |||
| Saturation, 23 ℃ | 0.13 | % | ISO 62 |
| Equilibrium, 23 ℃, 50% RH | 0.020 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 3140 | MPa | ASTM D638 |
| Tensile modulus | 2510 | MPa | ISO 527-1-2 |
| tensile strength | |||
| fracture | 49.0 | MPa | ASTM D638 |
| fracture | 53.0 | MPa | ISO 527-2/50 |
| yield | 61.0 | MPa | ISO 527-2/50 |
| yield | 52.0 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 7.3 | % | ASTM D638 |
| fracture | 8.0 | % | ISO 527-2/50 |
| yield | 3.6 | % | ASTM D638 |
| yield | 3.5 | % | ISO 527-2/50 |
| Bending modulus | 2420 | MPa | ISO 178 |
| 50 mm span | 2770 | MPa | ASTM D790 |
| bending strength | 89.0 | MPa | ISO 178 |
| bending strength | |||
| Yield, 50 mm span | 98.0 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 6.0 | kJ/m² | ISO 179/1eA |
| Impact strength of cantilever beam notch | ASTM D256 | ||
| -30℃ | 27 | J/m | ASTM D256 |
| 23℃ | 38 | J/m | ASTM D256 |
| Impact strength of cantilever beam notch | ISO 180/1A | ||
| -30℃ | 4.0 | kJ/m² | ISO 180-1A |
| 23℃ | 6.0 | kJ/m² | ISO 180-1A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 64 mm span | 92.0 | ℃ | ISO 75-2/Af |
| 1.8 MPa, unannealed, 3.2 mm | 90.0 | ℃ | ASTM D648 |
| Vicat Softening Temp | 110 | ℃ | ASTM D1525 10 |
| Vicat Softening Temp | |||
| B50 | 111 | ℃ | ISO 306 |
| B120 | 114 | ℃ | ISO 306/B120 |
| Linear coefficient of thermal expansion | |||
| TD：-40~40℃ | 7.4E-5 | 1/℃ | ISO 11359-2 |
| TD：-40~40℃ | 7.4E-5 | 1/℃ | ASTM E831 |
| MD：-40~40℃ | 7.4E-5 | 1/℃ | ASTM E831 |
| MD：-40~40℃ | 7.4E-5 | 1/℃ | ISO 11359-2 |
| Relative temperature index | |||
| Electrical performance | 65.0 | ℃ | UL 746 |
| Strength mechanical performance | 65.0 | ℃ | UL 746 |
| Impact mechanical performance | 65.0 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+14 to 1.5E+14 | ohms | ASTM D257 |
| Surface resistivity | 1.0E+14 to 1.5E+14 | ohms | IEC 60093 |
| Volume resistivity | 4.0E+16 to 4.5E+16 | ohms·cm | ASTM D257 |
| Volume resistivity | 4.0E+16 to 4.5E+16 | ohms·cm | IEC 60093 |
| Dielectric strength | |||
| 1.6 mm in oil | 29 | kV/mm | IEC 60243-1 |
| Dielectric constant | |||
| 1 MHz | 2.70 | ASTM D150 | |
| Relative permittivity | |||
| 1 MHz | 2.70 | IEC 60250 | |
| Dissipation factor | |||
| 1 MHz | 0.020 | ASTM D150 | |
| 1 MHz | 0.020 | IEC 60250 | |
| Compared to the leakage tracing index | PLC 3 | UL 746 | |
| Compared to the leakage tracing index | 250 | V | IEC 60112 |
| High Arc Burning Index (HAI) | PLC 0 | UL 746 | |
| Hot wire ignition | |||
| HWI | PLC 3 | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50 mm | V-1 | UL 94 | |
| Glowing wire flammability index | |||
| 3.0 mm | 960 | ℃ | IEC 60695-2-12 |
| Igniting temperature of the hot wire | IEC 60695-2-13 | ||
| 1 mm | 725 | ℃ | IEC 60695-2-13 |
| 2 mm | 725 | ℃ | IEC 60695-2-13 |
| 3 mm | 725 | ℃ | IEC 60695-2-13 |
| Extreme oxygen index | 30 | % | ISO 4589-2 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |