| About |
|---|
| NORYL FXN119BK is a low gloss PPE/HIPS grade. It provides a balance of mechanical properties and heat performance with intrinsic low gloss appreance. FXN119BKBK is available in black only.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PPO(PPE)+PS |
| Material Status | Commercial: Active |
| Features | Low Gloss,HB |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.06 | g/cm³ | ASTM D792 |
| Density | 1.06 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 280℃，5.0kg | 8.0 | g/10min | ASTM D1238 |
| Melt Volume Rate | |||
| 280℃，5 kg | 8.00 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.50 to 0.70 | % | Internal Method |
| Water absorption rate | |||
| Saturation, 23 ℃ | 0.23 | % | ISO 62 |
| Equilibrium, 23 ℃, 50% RH | 0.060 | % | ISO 62 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30℃ | 7.0 | kJ/m² | ISO 179/1eA |
| 23℃ | 14 | kJ/m² | ISO 179/1eA |
| Impact strength of cantilever beam notch | ASTM D256 | ||
| -30℃ | 110 | J/m | ASTM D256 |
| 23℃ | 160 | J/m | ASTM D256 |
| Impact strength of cantilever beam notch | ISO 180/1A | ||
| -30℃ | 7.0 | kJ/m² | ISO 180-1A |
| 23℃ | 11 | kJ/m² | ISO 180-1A |
| Dart impact equipped with measuring instruments | |||
| 23℃，Total Energy | 42.0 | J | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 64 mm span | 117 | ℃ | ISO 75-2/Af |
| 1.8 MPa, unannealed, 3.2 mm | 117 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed, 64 mm span | 133 | ℃ | ISO 75-2/Bf |
| Vicat Softening Temp | 140 | ℃ | ASTM D1525 10 |
| Vicat Softening Temp | |||
| B50 | 139 | ℃ | ISO 306 |
| B120 | 142 | ℃ | ISO 306/B120 |
| Ball pressure test | |||
| 125℃ | Pass | IEC 60695-10-2 | |
| Linear coefficient of thermal expansion | |||
| TD：-40~40℃ | 9.5E-5 | 1/℃ | ISO 11359-2 |
| TD：-40~40℃ | 9.5E-5 | 1/℃ | ASTM E831 |
| MD：-40~40℃ | 9.2E-5 | 1/℃ | ISO 11359-2 |
| MD：-40~40℃ | 9.2E-5 | 1/℃ | ASTM E831 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50 mm | HB | UL 94 | |
| Glowing wire flammability index | |||
| 3.2 mm | 750 | ℃ | IEC 60695-2-12 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 60 °, no texture | 20 | ASTM D523 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 2400 | MPa | ASTM D638 |
| Tensile modulus | 2200 | MPa | ISO 527-1-2 |
| tensile strength | |||
| fracture | 49.0 | MPa | ASTM D638 |
| fracture | 48.0 | MPa | ISO 527-2/50 |
| yield | 51.0 | MPa | ISO 527-2/50 |
| yield | 53.0 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 40 | % | ASTM D638 |
| fracture | 40 | % | ISO 527-2/50 |
| yield | 4.2 | % | ISO 527-2/50 |
| yield | 5.1 | % | ASTM D638 |
| Bending modulus | 2200 | MPa | ISO 178 |
| 50 mm span | 2200 | MPa | ASTM D790 |
| bending strength | 77.0 | MPa | ISO 178 |
| bending strength | |||
| Yield, 50 mm span | 85.0 | MPa | ASTM D790 |
| Taber abraser | |||
| 1000 cycles, 1000 g, CS-17 wheels | 75.0 | mg | Internal Method |
| Rockwell hardness | |||
| R-level | 116 | ISO 2039-2 | |
| Ball hardness | |||
| H358/30 | 95.0 | MPa | ISO 2039-1 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 70 to 90 | °C | |
| Drying time | 2.0 to 3.0 | hr | |
| Hopper temperature | 60 to 80 | °C | |
| Barrel rear temperature | 200 to 220 | °C | |
| Barrel middle temperature | 240 to 260 | °C | |
| Barrel front temperature | 260 to 285 | °C | |
| Nozzle temperature | 260 to 280 | °C | |
| Processing (melt) temperature | 265 to 285 | °C | |
| Mold temperature | 40 to 70 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |