NORYL™ GFN1520V resin

About
NORYL GFN1520V resin是一种聚苯醚+PS(PPE+PS)产品，含有的填充物为20%玻璃纤维增强材料，可以通过注射成型进行加工。

Product Description
Supplier	SABIC
Generic	PPO(PPE)+PS
Material Status	Commercial: Active
Features	Hydrolysis stability,Flame Characteristics

Technical Data
MECHANICAL	Nominal value	Unit	Test method
Bending modulus
2 mm/mim	5300	MPa	ISO 178
	5300	MPa	ASTM D790
bending strength
Yield, 2 mm/min	145	MPa	ISO 178
Yield, 1.30 mm/min, 50 mm span	140	MPa	ASTM D790
Tensile modulus	6200	MPa	ASTM D 638
1 mm/min	6400	MPa	ISO 527
5 mm/min	6200	MPa	ASTM D638
Tensile strain
	2.5	%	ISO 527
	2.5	%	ISO 527
	2.6	%	ASTM D638
	2.6	%	ASTM D638
tensile strength
Fracture, 5 mm/min	100	MPa	ISO 527
	100	MPa	ISO 527
	93	MPa	ASTM D638
	93	MPa	ASTM D638

IMPACT	Nominal value	Unit	Test method

23℃，80104 sp=62 mm	35	kJ/m²	ISO 179/1eU
-30 ℃, 80 * 10 * 4, 62 mm span	35	kJ/m²	ISO 179/1eU

-30℃	490	J/m	ASTM D 4812
23℃	490	J/m	ASTM D 4812
23℃，80104	30	kJ/m²	ISO 180/1U
-30°C，80104	30	kJ/m²	ISO 180/1U
Instrument impact total energy 23 ° C	16	J	ASTM D 3763
Impact strength of cantilever beam notch
-30℃	71	J/m	ASTM D256
23℃	83	J/m	ASTM D256

THERMAL	Nominal value	Unit	Test method
Ball pressure test
125℃±2℃	Passes		IEC 60695-10-2
Linear expansion coefficient
-40 ° C to 40 ° C, flow	3.E-05	1/°C	ASTM E 831
-40 ° C to 40 ° C, lateral	7.E-05	1/°C	ASTM E 831
-40 ° C to 40 ° C, flow	3.E-05	1/°C	ISO 11359-2
-40 ° C to 40 ° C, lateral	7.E-05	1/°C	ISO 11359-2
Vicat Softening Temp	140	℃	ASTM D1525
Vicat Softening Temp	140	℃	ISO 306
Hot deformation temperature
0.45 MPa, 64 mm span	140	℃	ISO 75/Bf
1.8 MPa, 64 mm span	130	℃	ISO 75/Af
1.8 MPa, unannealed, 3.2 mm	137	℃	ASTM D648

PHYSICAL	Nominal value	Unit	Test method
Water absorption rate
23℃，50% RH	0.06	%	ISO 62
Saturation, 23 ℃	0.2	%	ISO 62
Melt Volume Rate
280℃，10 kg	13	cm³/10min	ISO 1133
Melt Flow Rate
280℃，5 kg	15	g/10min	ASTM D1238
Shrinkage rate
MD：3.2 mm	0.2 – 0.4	%	Internal Method
TD：3.2 mm	0.3 – 0.6	%	Internal Method
Density	1.25	g/cm³	ISO 1183

Electrical performance	Nominal value	Unit	Test method
Dissipation factor
50-60 Hz	0.0008		IEC 60250
1 MHz	0.003		IEC 60250
Relative permittivity
50-60 Hz	2.9		IEC 60250
1 MHz	2.9		IEC 60250
Dielectric strength
3.2 mm in oil	18	kV/mm	IEC 60243-1
	5.0E+16	ohms	IEC 60093
Volume resistivity	>1.E+15	ohms·cm	IEC 60093

FLAME CHARACTERISTICS	Nominal value	Unit	Test method
Extreme oxygen index	26	%	ISO 4589
UL certification	1.5	mm	UL 94

Process Conditions
injection molding	Nominal value	Unit	Test method
drying temperature	100 – 120	°C
Drying time	2 – 3	hrs
Melt Temperature	280 – 300	°C
Nozzle temperature	260 – 280	°C
Front temperature	280 – 300	°C
Mid section temperature	260 – 280	°C
Post stage temperature	240 – 260	°C
Hopper temperature	60 – 80	°C
Mold temperature	80 – 120	°C

Notes
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.