| About |
|---|
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PPO(PPE)+PS |
| Material Status | Commercial: Active |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.30 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| TD：3.2 mm | 0.20-0.50 | % | ASTM D995 |
| MD：3.2 mm | 0.10-0.30 | % | ASTM D995 |
| Melt Flow Rate | |||
| 300℃，5.0kg | 10 | g/10min | ASTM D1238 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| Yield, 23 ℃ | 119 | MPa | ASTM D638 |
| 23℃ | 119 | MPa | ASTM D638 |
| Tensile strain | |||
| Yield, 23 ℃ | 2.6 | % | ASTM D638 |
| Fracture, 23 ℃ | 2.6 | % | ASTM D638 |
| Tensile modulus | |||
| 23℃ | 9100 | MPa | ASTM D638 |
| bending strength | |||
| Yield, 23 ℃ | 175 | MPa | ASTM D790 |
| Bending modulus | |||
| 23℃ | 7200 | MPa | ASTM D790 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 140 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed | 145 | ℃ | ASTM D648 |
| Vicat Softening Temp | 149 | ℃ | ASTM D1525 |
| Linear coefficient of thermal expansion | |||
| TD | 7.0E-5 | 1/℃ | ASTM D696 |
| MD | 3.0E-5 | 1/℃ | ASTM D696 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| All color | 3.00mm | HB | UL-94 |
| All color | 1.50mm | HB | UL-94 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 96 | J/m | ASTM D256 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 60-90 | °C | |
| Drying time | 2.0-6.0 | Hr | |
| Recommended moisture content | <=0.20 | % | |
| Barrel rear temperature | 220-260 | °C | |
| Barrel middle temperature | 230-270 | °C | |
| Barrel front temperature | 240-280 | °C | |
| Nozzle temperature | 250-290 | °C | |
| Mold temperature | 40-120 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |