| NORYL™ GFN1F resin PPE+PS blend. 10% Glass reinforced. NSF 61 listing in several colors (restrictions apply). FDA compliance (restrictions apply). Low water absorption. Hydrolytic stability. Dimensional stability. Suitable for fluid engineering applications including water filter and water meter components.&&NORYL™ GFN1F resin PPE+PS blend. 10% Glass reinforced. FDA compliance (restrictions apply). Low water absorption. Hydrolytic stability. Dimensional stability. Suitable for fluid engineering applications including water filter and water meter components.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PPO(PPE)+PS |
| Material Status | Commercial: Active |
| Features | Good Dimensional Stability,Hydrolysis stability,Low or no water absorption,HB |
| Availabilitys | North America,Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.13 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 300℃，5.0kg | 17 | g/10min | ASTM D1238 |
| Melt Volume Rate | |||
| 300℃，5 kg | 16.4 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.20 to 0.50 | % | Internal Method |
| Water absorption rate | |||
| 24hr | 0.060 | % | ASTM D570 |
| Weathering resistance | f1 | UL 746C | |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/2C | ||
| -30℃ | 9.0 | kJ/m² | ISO 179/2C |
| 23℃ | 11 | kJ/m² | ISO 179/2C |
| Charpy Unnotch Impact strength | ISO 179/1eU | ||
| -30℃ | 33 | kJ/m² | ISO 179/1eU |
| 23℃ | 35 | kJ/m² | ISO 179/1eU |
| Impact strength of cantilever beam notch | ASTM D256 | ||
| 23℃ | 450 | J/m | ASTM D4812 |
| -30℃ | 100 | J/m | ASTM D256 |
| 23℃ | 120 | J/m | ASTM D256 |
| Impact strength of cantilever beam notch | ISO 180/1A | ||
| -30℃ | 9.4 | kJ/m² | ISO 180-1A |
| 23℃ | 11 | kJ/m² | ISO 180-1A |
| Notched impact strength of cantilever beam | ISO 180/1U | ||
| -30℃ | 25 | kJ/m² | ISO 180/1U |
| 23℃ | 28 | kJ/m² | ISO 180/1U |
| Dart impact equipped with measuring instruments | |||
| 23℃，Total Energy | 21.7 | J | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 1.8 MPa, unannealed, 100 mm span | 124 | ℃ | ISO 75-2/Ae |
| 0.45 MPa, unannealed, 3.2 mm | 131 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed, 100 mm span | 132 | ℃ | ISO 75-2/Be |
| 1.8 MPa, unannealed, 3.2 mm | 122 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 6.4 mm | 125 | ℃ | ASTM D648 |
| Vicat Softening Temp | |||
| B50 | 131 | ℃ | ISO 306 |
| B120 | 134 | ℃ | ISO 306/B120 |
| Linear coefficient of thermal expansion | |||
| TD：-40~40℃ | 7.1E-5 | 1/℃ | ASTM E831 |
| MD：-40~40℃ | 5.1E-5 | 1/℃ | ASTM E831 |
| Relative temperature index | |||
| Electrical performance | 90.0 | ℃ | UL 746 |
| Strength mechanical performance | 90.0 | ℃ | UL 746 |
| Impact mechanical performance | 90.0 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Dielectric constant | |||
| 1 MHz | 2.90 | ASTM D150 | |
| Dissipation factor | |||
| 1 MHz | 1.4E-3 | ASTM D150 | |
| Arc resistance | PLC 7 | ASTM D495 | |
| High Arc Burning Index (HAI) | PLC 4 | UL 746 | |
| High voltage arc marking rate | |||
| HVTR | PLC 4 | UL 746 | |
| Hot wire ignition | |||
| HWI | PLC 5 | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50 mm | HB | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 4350 | MPa | ASTM D638 |
| Tensile modulus | 4400 | MPa | ISO 527-1-2 |
| tensile strength | |||
| fracture | 64.0 | MPa | ISO 527-2 |
| fracture | 63.0 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 3.0 | % | ISO 527-2 |
| fracture | 3.0 | % | ASTM D638 |
| Bending modulus | ASTM D790 | ||
| 50 mm span | 3840 | MPa | ASTM D790 |
| 100 mm span | 3590 | MPa | ASTM D790 |
| Bending modulus | 4160 | MPa | ISO 178 |
| bending strength | 122 | MPa | ISO 178 |
| bending strength | ASTM D790 | ||
| Yield, 50 mm span | 116 | MPa | ASTM D790 |
| Yield, 100 mm span | 108 | MPa | ASTM D790 |
| Rockwell hardness | |||
| Level L | 104 | ASTM D785 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 104 to 110 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Drying time, maximum | 8.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Recommended injection volume | 30 to 70 | % | |
| Barrel rear temperature | 260 to 304 | °C | |
| Barrel middle temperature | 271 to 310 | °C | |
| Barrel front temperature | 282 to 316 | °C | |
| Nozzle temperature | 293 to 316 | °C | |
| Processing (melt) temperature | 293 to 316 | °C | |
| Mold temperature | 77 to 104 | °C | |
| Back pressure | 0.345 to 0.689 | MPa | |
| Screw speed | 20 to 100 | rpm | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |