| About |
|---|
| NORYL™ GFN3 resin PPE+PS blend. 30% Glass reinforced. Low water absorption. Hydrolytic stability. Dimensional stability. Suitable for fluid engineering applications including pump housings, pump impellers and water meter components.&&NORYL™ GFN3 resin NORYL GFN3 is a standard 30 % glass filled material with a HDT/A of 145C according to ISO 75&&NORYL™ GFN3 resin PPE+PS blend. 30% Glass reinforced.FDA compliance (restrictions apply). Low water absorption. Hydrolytic stability. Dimensional stability. Suitable for fluid engineering applications including pump housings, pump impellers and water meter components.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PPO(PPE)+PS |
| Material Status | Commercial: Active |
| Features | Good Dimensional Stability,Hydrolysis stability,Low or no water absorption,HB |
| Availabilitys | North America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.29 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 300℃，5.0kg | 8.7 | g/10min | ASTM D1238 |
| Melt Volume Rate | |||
| 300℃，5 kg | 7.82 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.10 to 0.40 | % | Internal Method |
| Water absorption rate | |||
| 24hr | 0.060 | % | ASTM D570 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/2C | ||
| -30℃ | 12 | kJ/m² | ISO 179/2C |
| 23℃ | 13 | kJ/m² | ISO 179/2C |
| Charpy Unnotch Impact strength | ISO 179/1eU | ||
| -30℃ | 47 | kJ/m² | ISO 179/1eU |
| 23℃ | 39 | kJ/m² | ISO 179/1eU |
| Impact strength of cantilever beam notch | ASTM D256 | ||
| -30℃ | 120 | J/m | ASTM D256 |
| 23℃ | 120 | J/m | ASTM D256 |
| Impact strength of cantilever beam notch | ISO 180/1A | ||
| 23℃ | 590 | J/m | ASTM D4812 |
| -30℃ | 12 | kJ/m² | ISO 180-1A |
| 23℃ | 12 | kJ/m² | ISO 180-1A |
| Notched impact strength of cantilever beam | ISO 180/1U | ||
| -30℃ | 36 | kJ/m² | ISO 180/1U |
| 23℃ | 32 | kJ/m² | ISO 180/1U |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 1.8 MPa, unannealed, 64 mm span | 137 | ℃ | ISO 75-2/Af |
| 0.45 MPa, unannealed, 64 mm span | 143 | ℃ | ISO 75-2/Bf |
| 0.45 MPa, unannealed, 3.2 mm | 142 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed, 6.4 mm | 158 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 3.2 mm | 137 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 6.4 mm | 138 | ℃ | ASTM D648 |
| Vicat Softening Temp | |||
| B50 | 143 | ℃ | ISO 306 |
| B120 | 147 | ℃ | ISO 306/B120 |
| Linear coefficient of thermal expansion | |||
| TD：-40~40℃ | 6.2E-5 | 1/℃ | ASTM E831 |
| MD：-40~40℃ | 3.1E-5 | 1/℃ | ASTM E831 |
| Relative temperature index | |||
| Electrical performance | 90.0 | ℃ | UL 746 |
| Strength mechanical performance | 90.0 | ℃ | UL 746 |
| Impact mechanical performance | 90.0 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Dielectric strength | |||
| 3.2 mm in oil | 22 | kV/mm | ASTM D149 |
| Dielectric constant | ASTM D150 | ||
| 50 Hz | 2.93 | ASTM D150 | |
| 60 Hz | 2.93 | ASTM D150 | |
| Dissipation factor | ASTM D150 | ||
| 50 Hz | 9.0E-4 | ASTM D150 | |
| 60 Hz | 9.0E-4 | ASTM D150 | |
| Arc resistance | PLC 7 | ASTM D495 | |
| Compared to the leakage tracing index | PLC 4 | UL 746 | |
| High Arc Burning Index (HAI) | PLC 4 | UL 746 | |
| High voltage arc marking rate | |||
| HVTR | PLC 3 | UL 746 | |
| Hot wire ignition | |||
| HWI | PLC 4 | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50 mm | HB | UL 94 | |
| Extreme oxygen index | 26 | % | ASTM D2863 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 9150 | MPa | ASTM D638 |
| Tensile modulus | 8740 | MPa | ISO 527-1-2 |
| tensile strength | |||
| fracture | 116 | MPa | ASTM D638 |
| fracture | 117 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | 2.0 | % | ASTM D638 |
| fracture | 1.8 | % | ISO 527-2 |
| Bending modulus | ASTM D790 | ||
| 100 mm span | 7170 | MPa | ASTM D790 |
| 50 mm span | 8000 | MPa | ASTM D790 |
| Bending modulus | 8710 | MPa | ISO 178 |
| bending strength | 183 | MPa | ISO 178 |
| bending strength | ASTM D790 | ||
| Yield, 50 mm span | 180 | MPa | ASTM D790 |
| Yield, 100 mm span | 162 | MPa | ASTM D790 |
| Rockwell hardness | |||
| Level L | 108 | ASTM D785 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 110 to 121 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Drying time, maximum | 8.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Recommended injection volume | 30 to 70 | % | |
| Barrel rear temperature | 266 to 316 | °C | |
| Barrel middle temperature | 277 to 321 | °C | |
| Barrel front temperature | 288 to 327 | °C | |
| Nozzle temperature | 299 to 327 | °C | |
| Processing (melt) temperature | 299 to 327 | °C | |
| Mold temperature | 82 to 110 | °C | |
| Back pressure | 0.345 to 0.689 | MPa | |
| Screw speed | 20 to 100 | rpm | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |