| About |
|---|
| PPE + PS混合物。30％玻璃纤维增强。NSF 61列出了几种颜色（限制适用）。FDA合规（限制适用）。吸水率低 水解稳定性。 尺寸稳定性。适用于流体工程应用，包括泵壳体，泵叶轮和水表组件。 |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PPO(PPE)+PS |
| Material Status | Commercial: Active |
| Features | Low or no water absorption |
| Availabilitys | North America,Latin America |
| Technical Data | |||
|---|---|---|---|
| MECHANICAL | Nominal value | Unit | Test method |
| bending strength | |||
| Yield, 2 mm/min | 160 | MPa | ISO 178 |
| Yield, 1.30 mm/min, 50 mm span | 160 | MPa | ASTM D790 |
| Bending modulus | |||
| 2 mm/mim | 6800 | MPa | ISO 178 |
| 1.3 mm/min，50mm跨度 | 7200 | MPa | ASTM D790 |
| tensile strength | |||
| Fracture, Type I, 50 mm/min | 130 | MPa | ASTM D638 |
| Fracture, 50 mm/min | 110 | MPa | ISO 527 |
| Tensile strain | |||
| Fracture, Type I, 50 mm/min | 3 | % | ASTM D638 |
| Fracture, 50 mm/min | 2.5 | % | ISO 527 |
| Tensile modulus | |||
| 5 mm/min | 8600 | MPa | ASTM D638 |
| 1 mm/min | 8200 | MPa | ISO 527 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 590 | J/m | ASTM D4812 |
| 23℃ | 100 | J/m | ASTM D256 |
| -30℃ | 120 | J/m | ASTM D256 |
| 80*10*4，23℃ | 30 | kJ/m² | ISO 180-1U |
| 80*10*4 ，23℃ | 11 | kJ/m² | ISO 180-1A |
| 80*10*4，-30℃ | 10 | kJ/m² | ISO 180-1A |
| Instrument impact total energy | |||
| 23℃ | 20 | J | ASTM D 3763 |
| Charpy Notched Impact Strength | |||
| 80 * 10 * 4, 62mm span | 8 | kJ/m² | ISO 179/1eA |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, 64 mm span | 139 | ℃ | ISO 75/Af |
| 1.8 MPa, unannealed, 3.2 mm | 139 | ℃ | ASTM D256 |
| 0.45 MPa, unannealed, 3.2 mm | 147 | ℃ | ASTM D648 |
| Linear coefficient of thermal expansion | |||
| MD：-40~40℃ | 2.3E-05 | 1/℃ | ISO 11359-2 |
| MD：-40~40℃ | 2.1E-05 | 1/℃ | ASTM E 831 |
| TD：-40~40℃ | 7.5E-05 | 1/℃ | ASTM E 831 |
| TD：-40~40℃ | 7.E-05 | 1/℃ | ISO 11359-2 |
| Vicat Softening Temp | 149 | ℃ | ISO 306 |
| B50 | 147 | ℃ | ISO 306 |
| B50 | 147 | ℃ | ASTM D1525 |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | 1.31 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.1 – 0.4 | % | Internal Method |
| Melt Flow Rate | |||
| 280℃，5.0kg | 3.2 | g/10min | ASTM D1238 |
| Water absorption rate | |||
| Saturation, 23 ℃ | 0.1 | % | ISO 62 |
| 23℃，50% RH | 0.04 | % | ISO 62 |
| Melt Volume Rate | |||
| 280℃，5 kg | 2 | cm³/10min | ISO 1133 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 110 – 120 | °C | |
| Drying time | 3.0 – 4.0 | hr | |
| Drying time (cumulative) | 8.0 | hr | |
| Maximum moisture content | 0.020 | % | |
| Melt temperature | 300 – 325 | °C | |
| Nozzle temperature | 300 – 325 | °C | |
| Front temperature | 290 – 325 | °C | |
| Mid section temperature | 275 – 320 | °C | |
| Post stage temperature | 265 – 315 | °C | |
| Mold temperature | 80 – 110 | °C | |
| Back pressure | 0.3 – 0.7 | MPa | |
| Screw speed | 20 – 100 | MPa | |
| Shoot to cylinder size | 30 – 70 | % | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |