| About |
|---|
| PPE + PPS GF 30%, FR V-0&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PPS+PPE |
| Material Status | Commercial: Negative |
| Features | Flame Characteristics,V-0 |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.48 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 300℃，5.0kg | 44 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.30 to 0.70 | % | Internal Method |
| Water absorption rate | |||
| 24hr | 0.020 | % | ASTM D570 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| yield | 123 | MPa | Internal Method |
| Tensile strain | |||
| fracture | 10 | % | Internal Method |
| Bending modulus | 8620 | MPa | ASTM D790 |
| bending strength | 167 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 78 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 6.4 mm | 255 | ℃ | ASTM D648 |
| Linear coefficient of thermal expansion | |||
| MD：-30~30℃ | 1.8E-5 to 5.8E-5 | 1/℃ | ASTM E831 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+16 | ohms | ASTM D257 |
| Dielectric constant | ASTM D150 | ||
| 50 Hz | 3.30 | ASTM D150 | |
| 60 Hz | 3.30 | ASTM D150 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 0.80 mm | V-0 | UL 94 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Type 1A |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |