| About |
|---|
| NORYL APS* EXNX0080 resin is a glass filled, high performance blend of PPE/PPS that exhibits an excellent balance of high-heat resistance, strength, flame retardant, and conductivity. This grade can be electro-statically painted or powder coated without the need for a conductive primer. The resin is injection moldable and only available in black.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PPS+PPE |
| Material Status | Commercial: Negative |
| Features | Good Rigidity,Conductive,Sprayable,Flame Characteristics,High Heat Resistance |
| Availabilitys | North America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.62 | g/cm³ | ASTM D792 , ISO 1183 |
| Melt Flow Rate | |||
| 300℃，2.16kg | 16 | g/10min | ASTM D1238 |
| Melt Volume Rate | |||
| 300℃，2.16 kg | 10.0 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.30 to 0.80 | % | Internal Method |
| Water absorption rate | ISO 62 | ||
| Saturation, 23 ℃ | 0.020 | % | ISO 62 |
| Equilibrium, 23 ℃, 50% RH | 0.0 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| — | 16300 | MPa | ASTM D638 |
| — | 15000 | MPa | ISO 527-1-2 |
| tensile strength | |||
| yield | 79.2 | MPa | ASTM D638 |
| yield | 89.0 | MPa | ISO 527-2/5 |
| fracture | 79.2 | MPa | ASTM D638 |
| fracture | 89.0 | MPa | ISO 527-2/5 |
| Tensile strain | |||
| yield | 0.64 | % | ASTM D638 |
| yield | 0.64 | % | ISO 527-2/5 |
| fracture | 0.66 | % | ASTM D638 |
| fracture | 0.66 | % | ISO 527-2/5 |
| Bending modulus | |||
| 50 mm span | 12700 | MPa | ASTM D790 |
| — | 13600 | MPa | ISO 178 |
| bending strength | |||
| — | 0.980 | MPa | ISO 178 |
| Yield, 50 mm span | 118 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 35 | kJ/m² | ISO 179/1eA |
| Impact strength of cantilever beam notch | |||
| -30℃ | 37 | J/m | ASTM D256 |
| 23℃ | 34 | J/m | ASTM D256 |
| -30℃ | 34 | kJ/m² | ISO 180-1A |
| 23℃ | 34 | kJ/m² | ISO 180-1A |
| Dart impact equipped with measuring instruments | |||
| 23℃，Total Energy | 3.60 | J | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 3.2 mm | 234 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 100 mm span | 229 | ℃ | ISO 75-2/Ae |
| Vicat Softening Temp | |||
| B120 | 231 | ℃ | ASTM D1525 10 , ISO 306/B120 10 |
| B50 | 233 | ℃ | ISO 306 |
| Linear coefficient of thermal expansion | ASTM E831 , ISO 11359-2 | ||
| MD：-40~40℃ | 2.7E-5 | 1/℃ | ASTM E831，ISO 11359-2 |
| TD：-40~40℃ | 4.9E-5 | 1/℃ | ASTM E831，ISO 11359-2 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 2.5E+4 | ohms·cm | ASTM D257 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |