About |
---|
Blowmolding and extrusion. High heat and chemical resistant.&& |
Product Description | |
---|---|
Supplier | SABIC |
Generic | PPO(PPE)+PS+PA |
Material Status | Commercial: Negative |
Features | High Heat Resistance,Solvent resistance,HB |
Availabilitys | North America |
Technical Data | |||
---|---|---|---|
PHYSICAL | Nominal value | Unit | Test method |
Density | 1.09 | g/cm³ | ASTM D792 |
Shrinkage rate | |||
MD:3.2 mm | 1.3 to 1.4 | % | Internal Method |
MECHANICAL | Nominal value | Unit | Test method |
---|---|---|---|
tensile strength | |||
yield | 62.1 | MPa | ASTM D638 |
Tensile strain | |||
fracture | 83 | % | ASTM D638 |
Bending modulus | |||
100 mm span | 2280 | MPa | ASTM D790 |
bending strength | |||
Yield, 100 mm span | 95.8 | MPa | ASTM D790 |
IMPACT | Nominal value | Unit | Test method |
---|---|---|---|
Impact strength of cantilever beam notch | ASTM D256 | ||
-30℃ | 120 | J/m | ASTM D256 |
23℃ | 340 | J/m | ASTM D256 |
Dart impact equipped with measuring instruments | ASTM D3763 | ||
-30℃,Energy at Peak Load | 36.6 | J | ASTM D3763 |
23℃,Energy at Peak Load | 31.2 | J | ASTM D3763 |
THERMAL | Nominal value | Unit | Test method |
---|---|---|---|
Hot deformation temperature | |||
0.45 MPa, unannealed, 6.4 mm | 179 | ℃ | ASTM D648 |
Relative temperature index | 50.0 | ℃ | UL 746 |
Electrical performance | 50.0 | ℃ | UL 746 |
Impact mechanical performance | 50.0 | ℃ | UL 746 |
FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
---|---|---|---|
Flame retardant level | |||
1.50 mm | HB | UL 94 |
Process Conditions | |||
---|---|---|---|
Extrusion | Nominal value | Unit | Test method |
Drying temperature | 79 | °C | |
Drying time | 4.0 | hr | |
Barrel 1 zone temperature | 271 to 282 | °C | |
Barrel 2 zone temperature | 271 to 282 | °C | |
Barrel 3 zone temperature | 271 to 282 | °C | |
Barrel 4 zone temperature | 271 to 282 | °C | |
Barrel 5 zone temperature | 277 to 288 | °C | |
Connector temperature | 277 to 288 | °C | |
Nozzle temperature | 277 to 288 | °C |
Notes |
---|
1. Typical properties: these are not to be construed as specifications. |
2. Type I, 2.0 in/min |
3. 0.10 in/min |
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |